Product Description
High Elastic Thick Acrylic Waterproof Coating
Description
HCA-101 is a one component thick water-based polymer waterproof coating with high quality modified acrylic ester multicomponent copolymerized polymer emulsions as basic stock, added various auxiliary agents and fillers.
Where to use
Bathrooms;
Kitchens;
Balconies;
Floors.
Advantages
Water-based and eco-friendly emulsion without any organic solvents;
High intensity;
Good tensile strength and elongation;
Strong adaptability for substrate shrinkage, deformation and cracks;
Can be applied on wet substrates with tight bonding;
Available for one-time thick coating;
Ultraviolet radiation resisting, weather resisting and aging resisting;
Cold and convenient to apply.
Description
HCA-101 is a one component thick water-based polymer waterproof coating with high quality modified acrylic ester multicomponent copolymerized polymer emulsions as basic stock, added various auxiliary agents and fillers.
Where to use
Bathrooms;
Kitchens;
Balconies;
Floors.
Advantages
Water-based and eco-friendly emulsion without any organic solvents;
High intensity;
Good tensile strength and elongation;
Strong adaptability for substrate shrinkage, deformation and cracks;
Can be applied on wet substrates with tight bonding;
Available for one-time thick coating;
Ultraviolet radiation resisting, weather resisting and aging resisting;
Cold and convenient to apply.
| Item | Requirement | |
| Tensile strength, MPa ≥ | 1.5 | |
| Elongation at break, % ≥ | 300 | |
| Flexibility at low temperature, ° C | -20° C, no cracks | |
| Water tightness, 0.3MPa, 0.5h | Pass | |
| Drying time | Surface dry, h ≤ | 4 |
| Fully dry, h ≤ | 8 | |
| Solid content, % ≥ | 65 | |
| After ageing behavior tensile strength retention rate , % | Heat treatment ≥ | 80 |
| UV treatment ≥ | 80 | |
| Alkali treatment ≥ | 60 | |
| Acid treatment ≥ | 40 | |
| After ageing behavior elongation at break, % | Heat treatment ≥ | 200 |
| UV treatment ≥ | 200 | |
| Alkali treatment ≥ | 200 | |
| Acid treatment ≥ | 200 | |
| Heating distortion rate, % | Stretching ≤ | 1.0 |
| Shortening ≤ | 1.0 | |