Product Description
Basic information
Type: single wall
Continuous Temperature Range : -40ºC-125ºC
Radial Shrinking Ratio: 2:1 3:1
Color :optional
Longitudinal Shrinking Ratio: ±5%
Tensile Strength: ≥10.4MPa
Dielectric Voltage Withstand : 600V
Flammability: VW-1 UL94 V0
Concentricity : ≥65%
Application:The properties of environment-friendly, flexibility flame retardant, quick shrink and stable performance make them widely used in the field of electronics, communication, automotive, pipeline protection and so on. It is widely applied for connecting or end-handing, electric wire, insulating and harness of electric wire, corrosion and rust-proof of metallic rods or tubes, gas pipeline and marking for other products.
173
2000
17
Type: single wall
Continuous Temperature Range : -40ºC-125ºC
Radial Shrinking Ratio: 2:1 3:1
Color :optional
Longitudinal Shrinking Ratio: ±5%
Tensile Strength: ≥10.4MPa
Dielectric Voltage Withstand : 600V
Flammability: VW-1 UL94 V0
Concentricity : ≥65%
Application:The properties of environment-friendly, flexibility flame retardant, quick shrink and stable performance make them widely used in the field of electronics, communication, automotive, pipeline protection and so on. It is widely applied for connecting or end-handing, electric wire, insulating and harness of electric wire, corrosion and rust-proof of metallic rods or tubes, gas pipeline and marking for other products.
| inner diameter | wall thickness | shrink ratio | inner diameter after recovering |
| φ15 | 0.4mm | 2:1 | <7.5 |
| φ15 | 0.7mm | 2:1 | <7.5 |
| φ15 | 0.85mm | 2:1 | <7.5 |
| φ16 | 0.7mm | 2:1 | <8 |
| φ18 | 0.4mm | 2:1 | <9 |
| φ18 | 0.7mm | 2:1 | <9 |
| φ20 | 0.5mm/0.7mm | 2:1 | <10 |
| φ25 | 0.5mm/0.7mm | 2:1 | <12.5 |
| φ30 | 0.5mm/0.7mm | 2:1 | <15 |
| φ35 | 0.5mm/0.7mm | 2:1 | <17.5 |
| φ40 | 0.5mm/0.7mm | 2:1 | <20 |
| Special specifications, wall thickness can be customized. | |||