- Two versions.Bisphenol-A and Novolac epoxy modified vinylester resin.
- Medium viscosity, medium reactivity,
- Lighter color, with less foaming effect during the cure.
- Controlled exothermic peak.
- Good chemical and water resistance.
- Has promoted and thixotropic version.
- Has closed molding version.
- Has CIPP and tooling Gel coat base version.
Vinyl ester resin Application
- Hand lay up , spray up process, Filament winding, pul trusion,closed molding etc.
- Industrial parts with high chemical resistance, Pipes, tanks, containers etc.
Vinyl ester resin Package
- 200kg or 1000kg
- 6months for un-promoted or 3months for promoted under 25ºC,away from heat sources, direct sunlight or steam pipes,rain etc.
- Keep sealed to prevent moisture pick-up and monomer loss.
Vinyl ester resin Safety Attention
- Resin solutions contain volatile and flammable monomers such as styrene(flash point : 31ºC)
- The resin should be handled and used in well ventilated, flame proof areas
- To wear gloves and goggles to guard against any skin/ eye irritation arising from the presence of styrene. Under no circumstances must accelerators be mixed with peroxide catalysts as it can cause explosions.
- Transportation should according to the State Council "Chemistry Dangerous Articles Safety Management Regulations" due to it contains styrene monomer.
inflammable.
Bisphenol-A epoxy modified vinyl ester resin.
- Liquid resin characteristics.
| Item | Value |
| Appearance | Light yellow |
| Specific gravity at 25ºC | 1.05 - 1.10 g/cm3 |
| Viscosity at 25ºC | 300 - 500 mPa.s |
| Solid content | 55.0 - 65.0 % |
| Acid value | 4.0 - 11.0 mg KOH/g |
| Gel time | 10 - 60mins are available |
- Physical properties of casting resin
| Item | Value | Testing method |
| Barcol hardness | 42 | GB/T 3854 |
| Tensile strength | 91MPa | GB/T2568 |
| Tensile modulus | 3.5GPa | GB/T2568 |
| Tensile elongation | 6.3% | GB/T2568 |
| Flexural strength | 145MPa | GB/T 2570 |
| Flexural modulus | 3.6GPa | GB/T 2570 |
| HDT | 105ºC | GB/T 1634 |
Post cure condition: 2 hours at 80ºC, then 1 hrs at 120ºC.
Novolac epoxy modified vinyl ester resin
- Liquid resin characteristics.
| Item | Value |
| Appearance | Brown |
| Specific gravity at 25ºC | 1.05 - 1.10 g/cm3 |
| Viscosity at 25ºC | 300 - 500 mPa.s |
| Solid content | 60.0 - 67.0 % |
| Acid value | 4.0 - 11.0 mg KOH/g |
| Gel time | 10 - 60mins are available |
- Physical properties of casting resin
| Item | Value | Testing method |
| Barcol hardness | 44 | GB/T 3854 |
| Tensile strength | 80MPa | GB/T2568 |
| Tensile modulus | 3.9GPa | GB/T2568 |
| Tensile elongation | 3.0% | GB/T2568 |
| Flexural strength | 128MPa | GB/T 2570 |
| Flexural modulus | 3.9GPa | GB/T 2570 |
| HDT | 150ºC | GB/T 1634 |
Post cure condition: 2 hours at 80ºC, then 1 hrs at 120ºC
We focus on composites resin business and have a tolling plant in Changzhou city. We can supply all kinds of modified resin to feed up your solutions for composites. The business covers the total composites industry.
Q1:Do you provide sample for the trial?
A1:We could supply small size package for free.but we have to charge the freight.
Q2.Could you supply customized products friendly?
A2: Yes,we do.We have a team to sever in Fortune 500 and be able to supply products to satisfied with the end-users' technical requirement.
Q3. What about your lead time?
A3: Generally 2-4weeks after the order confirmed.
Q4. What are your terms of payment?
A4:Usually we do EXW, FOB, CIF, and DDP.