Product Description
PT90IR10 Pure Platinum Iridium tube shadow ring Ultra Fine Capillary Pipe Alloy Tubes
Platinum Iridium alloy is a high -temperature metal. it consists of two metals: platinum and Iridium, which has excellent performance such as high strength, high corrosion resistance and high melting point. Widely used in the aerospace industry, medical equipment and other fields. The shadow ring is a marker ring used for X -ray development marks in the remote working area during interventional therapy, which belongs to disposable medical materials;High melting point, corrosion resistance, good cold processing performance, high accuracy; In line with human biocompatibility,stable transmission information, can be implanted; Product specifications:OD:0.3-5.0mm,wall thickness:0.015-0.2mm,support non-standard customization.Materials: Pt90lr10.
Platinum Iridium alloy is a high -temperature metal. it consists of two metals: platinum and Iridium, which has excellent performance such as high strength, high corrosion resistance and high melting point. Widely used in the aerospace industry, medical equipment and other fields. The shadow ring is a marker ring used for X -ray development marks in the remote working area during interventional therapy, which belongs to disposable medical materials;High melting point, corrosion resistance, good cold processing performance, high accuracy; In line with human biocompatibility,stable transmission information, can be implanted; Product specifications:OD:0.3-5.0mm,wall thickness:0.015-0.2mm,support non-standard customization.Materials: Pt90lr10.
| OD mm | W.T. /mm | |||||||||||||
| ≥0.015 | ≥0.02 | ≥0.05 | ≥0.10 | ≥0.20 | ≥0.30 | ≥0.40 | ≥0.50 | ≥0.60 | ≥0.70 | ≥0.80 | ≥0.90 | ≥1.00 | ≥1.5 | |
| ≥0.3 | - | - | - | |||||||||||
| ≥0.5 | - | - | - | - | - | |||||||||
| ≥1.0 | - | - | - | - | - | - | - | |||||||
| ≥1.5 | - | - | - | - | - | - | - | - | - | |||||
| ≥2.0 | - | - | - | - | - | - | - | - | - | |||||
| ≥3.0 | - | - | - | - | - | - | - | - | - | - | ||||
| ≥4.0 | - | - | - | - | - | - | - | - | - | - | - | |||
| ≥5.0 | - | - | - | - | - | - | - | - | - | - | - | - | ||
| ≥6.0 | - | - | - | - | - | - | - | - | - | - | - | - | - | |
| ≥7.0 | - | - | - | - | - | - | - | - | - | - | - | - | - | |
| ≥8.0 | - | - | - | - | - | - | - | - | - | - | - | - | ||
| ≥9.0 | - | - | - | - | - | - | - | - | - | - | - | |||
| ≥10.0 | - | - | - | - | - | - | - | - | - | - | ||||
| ≥15.0 | - | - | - | - | - | - | - | - | - | |||||
| ≥20.0 | - | - | - | - | - | - | - | - | ||||||
| Material | Melting point (ºC) | Density (G/cm3) | Vickers hardnes Soft | Vickers hardnes Hard | Tensile force (MPa) | Resistivity (uΩ.cm)20ºC |
| Platinum (99.99%) | 1772 | 21.45 | 40 | 100 | 147 | 10.8 |
| Pt-Rh5% | 1830 | 20.7 | 70 | 160 | 225 | 17.5 |
| Pt-Rh10% | 1860 | 19.8 | 90 | 190 | 274 | 19.2 |
| Pt-Rh20% | 1905 | 18.8 | 100 | 220 | 480 | 20.8 |
| Platinum-Ir (99.99%) | 2410 | 22.42 | ||||
| Pure Platinum-Pt (99.99%) | 1772 | 21.45 | ||||
| Pt-Ir5% | 1790 | 21.49 | 90 | 140 | 174 | 19 |
| Pt-lr10% | 1800 | 21.53 | 130 | 230 | 382 | 24.5 |
| Pt-Ir20% | 1840 | 21.81 | 200 | 300 | 539 | 32 |
| Pt-lr25% | 1840 | 21.7 | 200 | 300 | 238 | 33 |
| Pt-Ir30% | 1860 | 22.15 | 210 | 300 | 242 | 32.5 |
| Pt-Ni10% | 1580 | 18.8 | 150 | 320 | 441 | 32 |
| Pt-Ni20% | 1450 | 16.73 | 220 | 400 | 588 | 34.1 |
| Pt-w% | 1850 | 21.3 | 200 | 360 | 588 | 62 |
| Applications: Gas sensors. Various sensors, medical components. Electric and heating probes, etc. | ||||||