Product Description
SuperMaker WH01 is an ABS like SL resin which has accurate and durable features. It is designed for solid state SLA platforms. SuperMaker WH01 can be applied in master patterns, concept models, general parts and functional prototypes in the field of automotive, medical and consumer electronics industries. The parts duability building with SuperMaker WH01 is over 6.5months. Typical features:
- Liquid resin`s medium viscosity, so easy recoating, easy clean parts and machines.
- Improved strength retained, improved dimensions retention of parts in humid condition.
- Need minimal part finishing.
- Long shelf life in machine.
Typical benefits:
- Need less part finishing time,easier post-curing.
- Building accurate and high tough parts with an improved dimensional stability.
- High quality controls for vacuum casting parts.
- Low shrink and good resistance to yellowing.
- Magnificent white color.
- Outstanding machinable SLA material.
Physical Properties - Liquid Material
| Appearance | White |
| Density | 1.11-~1.15g/cm3 @ 25 ºC |
| Viscosity | 400~480 cps @ 26 ºC |
| Dp | 0.135~0.158 mm |
| Ec | 7.8~8.6 mJ/cm2 |
| Building layer thickness | 0.05~0.12mm |
Mechanical Properties of Post-Cured Material
MEASUREMENT | TEST METHOD | VALUE |
| 90-minute UV post-cure | ||
| Hardness , Shore D | ASTM D 2240 | 78~87 |
| Flexural modulus , Mpa | ASTM D 790 | 2,742-2,855 |
| Flexural strength , Mpa | ASTM D 790 | 69- 77 |
| Tensile modulus , MPa | ASTM D 638 | 2,638-2,735 |
| Tensile strength , MPa | ASTM D 638 | 41-58 |
| Elongation at break | ASTM D 638 | 8 -11% |
| Poisson`s Ratio | ASTM D 638 | 0.4-0.44 |
| Impact strength notched Izod, J/m | ASTM D 256 | 30- 36 |
| Heat deflection temperature, ºC | ASTM D 648 @66PSI | 46~60 |
| Glass transition,Tg ,ºC | DMA,E"peak | 47~64 |
| CoEHficient of thermal expension, /ºC | TMA(T<Tg) | 89~101*E-6 |
| Density , g/cm3 | 1.12~1.18 | |
Dielectric Constant 60 Hz | ASTM D 150-98 | 4.2~5.0 |
Dielectric Constant 1 kHz | ASTM D 150-98 | 3.3~4.2 |
Dielectric Constant 1 MHz | ASTM D 150-98 | 3.2~4.0 |
Dielectric Strength kV/mm | ASTM D 1549-97a | 12.8~16.1 |