Asbestos joint sheet
Asbestos joint sheet is made of good long asbestos fiber, oil-resistance synthetic rubber, heat-resisting packing material compound heating and compression molding it and used as sealing material in the joints of oil pipeline and sealing gasket used on automobiles motorcycles, agricultural machinery, engineering machinery engines it widely used as the sealing gasket material for the equipment in kerosene, petrochemical, alkali, acid, solvent, fuel oil, petroleum-based lubricating oil and other mediums.
We can supply temperature from 150 degree up to 600 degree. Max size 1500 x 4000 mm from thickness 0.4 mm - 6.0 mm.
Asbestos joint sheet is made of good long asbestos fiber, oil-resistance synthetic rubber, heat-resisting packing material compound heating and compression molding it and used as sealing material in the joints of oil pipeline and sealing gasket used on automobiles motorcycles, agricultural machinery, engineering machinery engines it widely used as the sealing gasket material for the equipment in kerosene, petrochemical, alkali, acid, solvent, fuel oil, petroleum-based lubricating oil and other mediums.
We can supply temperature from 150 degree up to 600 degree. Max size 1500 x 4000 mm from thickness 0.4 mm - 6.0 mm.
| Item | RS500 | RS400 | RS350 | RS300 | RS200 | RS150 |
| Temperature ( °C ) | 500 | 400 | 350 | 300 | 200 | 150 |
| Pressure (MPa) | 12 | 9 | 8 | 5 | 3 | 2 |
| Tensile strength (MPa ≥ ) | 19 | 15 | 12 | 9 | 6 | 5 |
| Aging coefficient | 0.9 | 0.9 | 0.9 | 0.9 | 0.9 | 0.9 |
| Density (g/cm3) | 1.6~2.0 | 1.6~2.0 | 1.6~2.0 | 1.6~2.0 | 1.6~2.0 | 1.6~2.0 |
| Compressibility (%) | 12 ± 5 | 12 ± 5 | 12 ± 5 | 12 ± 5 | 12 ± 5 | 12 ± 5 |
| Rebound degree ( ≥ %) | 45 | 45 | 40 | 40 | 35 | 35 |
| Pliability | No Crack | No Crack | No Crack | No Crack | No Crack | No Crack |
| Stress-relaxation ≤ | 50 | 50 | 50 | 50 | 50 | 50 |
| Steam Airtightness | with the temperature of 490~500 °C and the pressure of 11-12 MPa , keeping for 30 min without puncture | with the temperature of 390~400 °C and the pressure of 8-9 MPa , keeping for 30 min without puncture | with the temperature of 340~350 °C and the pressure of 7-8 MPa , keeping for 30 min without puncture | with the temperature of 290~300 °C and the pressure of 4-5 MPa , keeping for 30 min without puncture | with the temperature of 200~220 °C and the pressure of 2-3 MPa , keeping for 30 min without puncture | with the temperature of 140~150 °C and the pressure of 1.5-2 MPa , keeping for 30 min without puncture |