High Tensile Strength Heat Shrink Sleeve
Experience the ultimate in durability and insulation with our High Tensile Strength Heat Shrink Sleeve. Made from cross-linked modified polyolefin, this versatile shrink sleeve is designed to withstand extreme temperatures ranging from -55ºC to 125ºC.
With a shrink ratio of 2:1, our heat shrink sleeve provides a secure and seamless fit, ensuring excellent insulation, heat resistance, and voltage performance. Its soft and flexible nature allows for easy installation and maneuverability.
Rest assured, our product is manufactured in compliance with "RoHS" and "REACH" standards, making it a safe and environmentally friendly choice. It is also UL224 VW-1 flammability rated, providing added peace of mind.
Widely used in electronics, subways, buildings, public facilities, and more, our heat shrink sleeve is the go-to solution for all your cable protection needs.
Choose the High Tensile Strength Heat Shrink Sleeve from Suzhou Antongtai New Material Technology Co., Ltd. for a reliable and efficient solution that meets the highest industry standards.
| Test Items | Test Methods | Performance |
| Temperature Rating | UL224 | 125ºC |
| Length Rate Of Change | ASTM D2671 | -5ºC~+5ºC |
| Tensile Strength | ASTM D638 | ≥10.4MPa |
| Breaking Elongation | ASTM D638 | ≥200% |
| Hot Air Aging Test | 158.0ºC/168h | - |
| Thermal Aging Tensile Strength | ASTM D638 | ≥7.3MPa |
| Heat Aging Breaking Elongation | ASTM D638 | ≥100% |
| Voltage Level | UL224 | 300V/600V |
| Volume Resistivity | ASTM D2671 | ≥1.0x1012cm |
| Breakdown Voltage | UL224 | 2500V(60s) No Breakdown |
| Thermal Stock | UL224/250ºC±3ºC/4h | Does not drip, Does not flow, Does not crack |
| With heart | ASTM D2671 | ≥70% |
Size | As supplied (mm) | after full Recovery(mm) | ||
Diameter(D) | Thickness(T) | Diameter(d) | Thickness(t) | |
2:1 | ||||
Ф0.7 | 1.0+0.2/-0.1 | 0.18±0.05 | ≤0.40 | 0.32±0.08 |
Ф0.8 | 1.2+0.2/-0.1 | 0.18±0.05 | ≤0.45 | 0.34±0.08 |
Ф1.0 | 1.5+0.2/-0.1 | 0.18±0.05 | ≤0.60 | 0.36±0.08 |
Ф1.5 | 2.1+0.2/-0.1 | 0.18±0.05 | ≤0.80 | 0.36±0.08 |
Ф2.0 | 2.5+0.2/-0.1 | 0.20±0.05 | ≤1.00 | 0.42±0.08 |
Ф2.5 | 3.0+0.2/-0.1 | 0.22±0.05 | ≤1.25 | 0.46±0.08 |
Ф3.0 | 3.5+0.2/-0.1 | 0.22±0.05 | ≤1.50 | 0.46±0.08 |
Ф3.5 | 4.0+0.2/-0.1 | 0.22±0.05 | ≤1.75 | 0.46±0.08 |
Ф4.0 | 4.6+0.2/-0.1 | 0.22±0.05 | ≤2.00 | 0.46±0.08 |
Ф4.5 | 5.0+0.2/-0.1 | 0.23±0.05 | ≤2.25 | 0.46±0.08 |
Ф5.0 | 5.5+0.2/-0.1 | 0.25±0.05 | ≤2.50 | 0.50±0.08 |
Ф5.5 | 6.0+0.2/-0.1 | 0.25±0.05 | ≤2.75 | 0.50±0.08 |
Ф6.0 | 6.5+0.2/-0.1 | 0.25±0.05 | ≤3.00 | 0.55±0.10 |
Ф6.5 | 6.9+0.2/-0.1 | 0.25±0.05 | ≤3.25 | 0.55±0.10 |
Ф7.0 | 7.5+0.2/-0.1 | 0.25±0.05 | ≤3.50 | 0.55±0.10 |
Ф8.0 | 8.5+0.3/-0.1 | 0.28±0.06 | ≤4.00 | 0.58±0.10 |
Ф9.0 | 9.5+0.2/-0.1 | 0.28±0.06 | ≤4.50 | 0.58±0.10 |
Ф10 | 10.5+0.3/-0.1 | 0.28±0.06 | ≤5.00 | 0.58±0.10 |
Ф11 | 11.5+0.3/-0.1 | 0.28±0.06 | ≤5.50 | 0.58±0.10 |
Ф12 | 12.5+0.3/-0.1 | 0.28±0.06 | ≤6.00 | 0.58±0.10 |
Ф13 | 13.5+0.3/-0.1 | 0.28±0.06 | ≤6.50 | 0.58±0.10 |
Ф14 | 14.5+0.3/-0.1 | 0.28±0.06 | ≤7.00 | 0.58±0.10 |
Ф15 | 15.5+0.3/-0.1 | 0.28±0.06 | ≤7.50 | 0.58±0.10 |
Ф16 | 16.5+0.3/-0.1 | 0.28±0.06 | ≤8.00 | 0.58±0.10 |
Ф17 | 17.5+0.3/-0.1 | 0.28±0.06 | ≤8.50 | 0.58±0.10 |
Ф18 | 18.5+0.3/-0.1 | 0.32±0.08 | ≤9.00 | 0.68±0.10 |
Ф20 | 20.6+0.5/-0.2 | 0.32±0.08 | ≤10.0 | 0.68±0.10 |
Ф22 | 22.6+0.7/-0.2 | 0.35±0.08 | ≤11.0 | 0.72±0.12 |
Ф25 | 25.6+0.7/-0.2 | 0.40±0.10 | ≤12.5 | 0.78±0.12 |
Ф28 | 28.6+0.7/-0.2 | 0.40±0.10 | ≤14.0 | 0.78±0.12 |
Ф30 | 30.6+0.7/-0.2 | 0.40±0.10 | ≤15.0 | 0.82±0.12 |
Ф35 | 35.6+0.7/-0.2 | 0.45±0.10 | ≤17.5 | 0.92±0.12 |
Ф40 | 41.0±0.5 | 0.50±0.12 | ≤20.0 | 1.00±0.15 |
Ф45 | 46.0±0.5 | 0.50±0.12 | ≤22.5 | 1.00±0.15 |
Ф50 | 51.0±1.0 | 0.55±0.15 | ≤25.0 | 1.10±0.15 |
Ф55 | 55.5±1.0 | 0.55±0.15 | ≤27.5 | 1.10±0.15 |
Ф60 | 60.5±1.0 | 0.60±0.15 | ≤30.0 | 1.25±0.20 |
Ф70 | 71.0±1.0 | 0.60±0.15 | ≤35.0 | 1.25±0.20 |
Ф80 | 81.0±1.0 | 0.60±0.15 | ≤40.0 | 1.25±0.20 |
Ф90 | 91.0±1.0 | 0.60±0.15 | ≤45.0 | 1.25±0.20 |
Ф100 | 101.0±1.0 | 0.60±0.15 | ≤50.0 | 1.25±0.20 |
Note: Other sizes and colors can be available upon request | ||||