TEMPMAX® ALUMINA FIBER BOARD / Polycrystalline Wool Board
TempMax® alumina fiber board is manufactured in a wet forming process using TempMax® alumina fiber bulk and binders. TempMax® alumina fiber board has excellent thermal stability at very high operating temperatures. TempMax® alumina fiber board can reduce energy costs and cycling times due to high insulating capability, as well as serving to protect refractory surfaces from thermal shock and chemical attack.
Features
Excellent thermal shock resistance
Can be machined, cut and shaped easily
High rigidity and light weight
Low thermal conductivity
Low heat storage
Typical Applications
High-temperature laboratory
High-temperature furnaces and kilns
Aerospace industry
Back-up insulation to dense refractory linings
Expansion joints
Typical Parameters
Description | TEMPMAX® 140 BOARD | TEMPMAX® 145 BOARD | TEMPMAX® 160 LD BOARD | TEMPMAX® 160 HD BOARD |
Classification Temperature (ºC ) | 1600 | 1600 | 1700 | 1700 |
Continuous Temperature Use Limit (ºC ) | 1400 | 1450 | 1600 | 1600 |
Chemical Composition (%) | ||||
Al2O3 | 60 | 62 | 70 | 70 |
Al2O3+SiO2 | 98 | 98 | 98.5 | 98.5 |
Color | White | White | White | White |
Density (kg/m³) | 300 | 300 | 250 | 400 |
Modules of Rupture (MPa) | ≥0.3 | ≥0.3 | ≥0.3 | ≥0.3 |
Compressive Strength (MPa, 10% relative deformation) | 0.25 | 0.25 | 0.15 | 0.3 |
Loss of Ignition (%) | ≤8 | ≤8 | ≤8 | ≤8 |
Permanent Linear Shrinkage (%) | 1400ºC x 24h ≤2.0 | 1450ºC x 24h ≤2.0 | 1600ºC x 24h ≤1.5 | 1600ºC x 24h ≤1.5 |
Thermal Conductivity (W/m·K) | ||||
400ºC | 0.08 | 0.08 | 0.08 | 0.08 |
600ºC | 0.10 | 0.10 | 0.12 | 0.09 |
800ºC | 0.13 | 0.13 | 0.14 | 0.12 |
1000ºC | 0.16 | 0.15 | 0.17 | 0.15 |
1200ºC | 0.19 | 0.19 | 0.20 | 0.19 |