PARA-Aramid Fiber
Anti-Pilling, Abrasion-Resistant, Flame Retardant, Anti-Distortion, Heat-Resistant, Bullet Proof
Pulp
Yellow
High Strength Fiber
Miscellaneous Chain Synthetic
1f1710
Yellowish
PARA-Aramid
1.47g/cm3
100%
1.13-1.32mm
(5.00-10.00)M2/G
(-1.00-0)Kv
(30.0-35.0).Sr
<0.2%
XIANGU
5kg Per Bag
ROHS
Guangdong
54021190
Product Description
Kevlar Pulp Dupont 1F1710 1F538 for Sealing Material was made of P-aramid fiber by surface fibrillation treatment.It has a larger surface area,its unique surface structure greatly improved in grip of the mixture, this fiber has high strength and modulus,strong hydrogen bonding strength,chemical solvent resistance,anti-acid and alkali, anti-aging,good adhesion with rubber,therefore it is a suitable reinforcing fiber applied to friction and sealing products.Usually it is used as a reinforcing material,widely used in rubber, thermoplastics,thermosetting plastics,various high-temperature composite structures, brake pads, clutch linings,friction belt,wear-resistant filler,gaskets, slot insulation, phase barrier insulation, interturn insulation and so on. It can also be used wet paper making or other synthetic insulating paper.
SPECIFICATIONS:
APPLICATION FIELDS:
1.Engineering Plastics,thermosetting resin,friction materials, automotive brakes,composite materials and Kevlar reinforced paper.
2.reinforcing materials,construction,rubber,reinforced cable,cable and other high-intensity rope.
3.composite material with resin or rubber,can significantly reduce the weight,increase loading weight,suitable for the production of aerospace equipment,high-speed trains and yachts shell.
4.Friction and sealing materials,friction materials reinforced fiber, significantly improved wear resistance,suitable for high temperature conditions.
STORAGE:
The kevlar pulp should be keep dry in their original bags and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire.
PACKAGING:
PRODUCT DETAILED IMAGES:
SPECIFICATIONS:
| Model: | 1F1710 |
| Color: | yellowish |
| Fiber type: | Para-aramid |
| Content of P-fiber: | 100% |
| Average fiber length: | (1.13-1.32)mm |
| Specific surface: | (5.00-13.00)m2/g |
| Moisture: | (8.1-11)% |
| Net weight: | 5.00kg/bag |
APPLICATION FIELDS:
1.Engineering Plastics,thermosetting resin,friction materials, automotive brakes,composite materials and Kevlar reinforced paper.
2.reinforcing materials,construction,rubber,reinforced cable,cable and other high-intensity rope.
3.composite material with resin or rubber,can significantly reduce the weight,increase loading weight,suitable for the production of aerospace equipment,high-speed trains and yachts shell.
4.Friction and sealing materials,friction materials reinforced fiber, significantly improved wear resistance,suitable for high temperature conditions.
STORAGE:
The kevlar pulp should be keep dry in their original bags and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire.