Product Description
Geomax® Geosynthetics (since 2006) on the exhibition hosted by IGS
HDPE Material Price Chart(Enquiry Us to Get Your Latest Guotation)
HDPE Geomembrane Datasheet (Smooth)
HDPE Geomembrane Datasheet (Smooth)
Properties | Test Method | Test Value | ||||||||
| 0.5 mm | 0.75mm | 1.00 mm | 1.25 mm | 1.50 mm | 2.00 mm | 2.50 mm | 3.00 mm | |||
| Maximum Deviation of thickness | -15% | -15% | -15% | -15% | -15% | -15% | -15% | -15% | ||
| Density (min. ave.) | D 1505/D792 | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | |
| Tensile Properties(min.ave) | Yield strength Break strength | D6693 | 8N/mm | 11 N/mm | 15 N/mm | 18 N/mm | 22 N/mm | 29 N/mm | 37 N/mm | 44 N/mm |
| 14N/mm | 20N/mm | 27 N/mm | 33 N/mm | 40 N/mm | 53N/mm | 67 N/mm | 80 N/mm | |||
| Yield elongation | 12% | 12% | 12% | 12% | 12% | 12% | 12% | 12% | ||
| Break elongation | 700% | 700% | 700% | 700% | 700% | 700% | 700% | 700% | ||
| Tear Resistance (min. ave.) | D 1004 | 63 N | 93 N | 125 N | 156 N | 187 N | 249 N | 311 N | 374 N | |
| Puncture Resistance (min. ave.) | D 4833 | 160N | 240N | 320 N | 400 N | 480 N | 640 N | 800 N | 960 N | |
| Carbon Black Content (range) | D 4218 | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | |
| Oxidative Induction Time (OIT) (min.ave.) Standard OIT | D 3895 | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | |
| Oven Aging at 85°C Standard OIT (min. ave.) - % retained after 90 days | D 5721 D 3895 | 55% | 55% | 55% | 55% | 55% | 55% | 55% | 55% | |
| UV Resistance High Pressure OIT (min. ave.) - % retained after 1600 hrs | D 3895 D 5885 | 50% | 50% | 50% | 50% | 50% | 50% | 50% | 50% | |
HDPE Geomembrane Datasheet (Textured)
| Test Properties | Unit | Standard | Test frequency | GM10 | GM15 | GM20 | GM25 |
| Thickness | mm | D5994 | per roll | 1.00 | 1.50 | 2.00 | 2.50 |
| Asperity Height | mm | D7446 | Every 2nd roll (2) | 0.25 | |||
| Density | g/cc | D1505/D792 | 90,000kg | 0.94 | |||
| Tensile Properties | |||||||
| Yield Strength | KN/m | D6693 Type IV | 9,000 kg | 15 | 22 | 29 | 37 |
| Break Strength | KN/m | 10 | 16 | 21 | 26 | ||
| Yield Elongation | % | 12 | 12 | 12 | 12 | ||
| Break Elongation | % | 100 | 100 | 100 | 100 | ||
| Tear Resistance | N | D1004 | 20,000kg | 125 | 187 | 249 | 311 |
| Puncture Resistance | N | D4883 | 20,000kg | 267 | 400 | 534 | 667 |
| Stress Crack Resistance | hr | D5397(App) | per GRI GM-10 | 300 hr | |||
| Carbon black content | % | D4218 | 9,000kg | 2.0-3.0% | |||
| Carbon black dispersion | / | D5596 | 20,000kg | For 10 different views: 9 in Categories 1 or 2 and 1 in Category 3 | |||
| Oxidative Induction Time | |||||||
| Standard OIT | min | D3895 | 90,000kg | 100 min | |||
| High pressure OIT | / | D5885 | 90,000kg | 400 min | |||
| Oven Aging at 85°C retained after 90 days | % | D5721 | per each formulation | 55% | |||
| Standard OIT | / | D3895 | 80% | ||||
| High pressure OIT | / | D5885 | 80% | ||||
| UV Resistance | |||||||
| High Pressure OIT - % retained after 1600 hrs | % | D5885 | per each formulation | 50% | |||
| Roll Width | m | / | / | 7 | 7 | 7 | 7 |
| Roll Length | m | / | / | 210 | 140 | 105 | 70 |
| Size stability | % | / | / | 2% | |||
Packing
certification
FAQ:
FAQ
1. How about the delivery time?
Lead time: 1-3 weeks on receipt of 30% T/T deposit.
2. What's is the MOQ?
2000m2 or negotiate
3. How to deal with the sample charge?
Samples are free, and we only charge the freight. We will return the sample freight in the future order.
4. Can you produce the product according to customers' requirements?
Sure, we are a professional manufacturer, OEM and ODM are both welcome.