Audited Supplier
Mflam 1430
66034- 17- 1
REACH, RoHS
Yes
White
Plastic Flame Retardant
Powder
PP-GF, PP, PE
UL94_V0
Less Than 210 Degrees Celsius
16%-20%
18%-22%
Mflam
25kg Paper Bag, 17.5mt/20'fcl
Piperazine Pyrophosphate
China
3824999999
Product Description
Non Halogen Flame Retardant for Pure PP PP+GF-30 Compounding
Specification:
| Item | Index | |
| Appearance | White Powder | |
| The Content of Phosphorus %(W/W) | 18±2 | |
| The Content of Nitrogen %(W/W) | 20±2 | |
| Particle Size D50 (μm) D90(um) | 5±3 15±4 | |
| Moisture %(W/W) | ≤0.5 | |
| TGA (20ºC/min, in N2) | Weight Loss 1% | ≥250ºC |
| Weight Loss 5% | ≥290ºC | |
| Recommend Process Condition ºC | ≤ 210 | |
Application:
Mflam 1430 is a halogen-free intumescent flame retardant for polyolefins, especially for PP glass fiber reinforced. PP treated by Mflam 1430, can reach UL 94 V-0 (0.8mm), and pass the 70 °C X168 hours water immersion test (UL746C), while passing GWIT 900 ° C and GWFI 960 ° C glow wire test. Mflam 1430 can also be applied to glass fiber reinforced PP, can reach UL 94 V-0 (0.8mm).
In TPE application, Mflam 1430 is also a very good choice.
Advantage:
Mflam 1430 is especially for glass fiber reinforce PP, and the PP which have the high requirement of high temperature and water solubility.
Another advantage of Mflam 1430 is: the PP made by Mflam 1430 can replace of PC/ABS engine plastic, same function, lower cost.
Recommended dosage:
| Polymer | pp | PE |
| Mflam 1430 Dosage% | 3.2mm: 15-20% 1.6mm: 22-25% 0.8mm: 22-30% | 3.2mm: 18-23% 1.6mm: 23-28% 0.8mm: 25-33% |
| Flame Retardancy | UL 94 V-0, 5VA | |
PS: it can be added 10-30% fiber glass in PP.
Shipping Information:
The package is 25kg craft paper bag or on customer's request, and can be loaded 17.5mt with pallet in 1x 20'FCL.
Remarks:
(1) The initial thermal decomposition temperature of Mflam 1430 in air is about 280 °C, so the processing temperature of the twin-screw can be adjusted according to the specific conditions to enhance the dispersion and enhance the plasticization effect. A certain degree of hollowness must be maintained during the twin-screw extrusion process.
(2) When Mflam 1430 is used in PP, it is not recommended to use a combination of strong shear screws.