Audited Supplier
Hastelloy 556
Aviation, Electronics, Industrial, Medical, Chemical
JIS, GB, DIN, BS, ASTM, AISI
Alloy
Nickel Bar
Not Powder
Mingson
Wooden Crate
As customers's request
China
7505120000
Product Description
R30556 combines effective resistance to sulfidizing, carburizing and chlorine-bearing environments at high temperatures with good oxidation resistance, fabricability and excellent high temperature strength. It also resists to corrosion by molten zinc, molten chloride salts and other salts.
CHEMICAL COMPOSITION
CHEMICAL COMPOSITION
| C | Mn | Fe | P | S | Si | Cu | Ni | Co | Al | Ti | Cr | Nb+Ta | Mo | B | N | W | La | V | Nb | |
| Hastelloy B | ≤0.05 | ≤1.0 | 4.0-6.0 | ≤0.04 | ≤0.03 | ≤1.0 | balance | ≤2.5 | ≤1.0 | 26.0-30.0 | 0.2-0.4 | |||||||||
| Hastelloy B-2 | ≤0.01 | ≤1.0 | ≤2.0 | ≤0.02 | ≤0.03 | ≤0.01 | balance | ≤1.0 | 0.04-0.07 | 26.0-30.0 | ||||||||||
| Hastelloy C | ≤0.08 | ≤1.0 | 4.0-7.0 | ≤0.04 | ≤0.03 | ≤1.0 | 50.0-58.0 | 14.5-16.5 | 15.0-17.0 | |||||||||||
| Hastelloy C-4 | ≤0.015 | ≤1.0 | ≤3.0 | ≤0.04 | ≤0.03 | ≤0.08 | balance | ≤2.0 | ≤0.7 | 14.0-18.0 | 14.0-17.0 | |||||||||
| Hastelloy C-22 | ≤0.015 | ≤0.5 | 2.0-6.0 | ≤0.02 | ≤0.35 | ≤0.08 | balance | ≤2.5 | 20.0-22.5 | 12.5-14.5 | 2.5-3.5 | 0.02 | ||||||||
| Hastelloy C-276 | ≤0.08 | ≤1.0 | 4.0-7.0 | ≤0.04 | ≤0.03 | ≤1.0 | balance | ≤2.5 | 14.5-16.5 | 15.0-17.0 | 3.0-4.5 | ≤0.35 | ||||||||
| Hastelloy C-2000 | ≤0.01 | ≤0.5 | ≤3.0 | ≤0.025 | ≤0.01 | ≤0.08 | 1.3-1.9 | balance | ≤2.0 | ≤0.5 | 22.0-24.0 | 15.0-17.0 | ||||||||
| Hastelloy G-30 | ≤0.03 | 0.3-1.5 | 13.0-17.0 | ≤0.04 | ≤0.02 | 0.2-0.8 | 1.0-2.4 | balance | ≤5.0 | 28.0-31.5 | 4.0-6.0 | 1.5-4.0 | 0.3-1.5 | |||||||
| Hastelloy G-35 | ≤0.05 | ≤0.5 | ≤2.0 | ≤0.03 | ≤0.015 | ≤0.6 | ≤0.30 | balance | ≤1.0 | ≤0.4 | 32.25-34.25 | 7.6-9.0 | ≤0.6 | ≤0.2 | ||||||
| Hastelloy X | 0.05-0.15 | ≤1.0 | 17.0-20.0 | ≤0.04 | ≤0.03 | ≤1.0 | balance | 0.5-2.5 | 20.5-23.0 | 8.0-10.0 | 0.2-1.0 | |||||||||
| Hastelloy S | ≤0.02 | 0.3-1.0 | ≤3.0 | ≤0.02 | ≤0.015 | 0.2-0.75 | balance | ≤2.0 | 0.1-0.5 | 14.5-17.0 | 14.0-16.5 | ≤1.0 | 0.01-0.1 |
PHYSICAL PROPERTIES
| Alloy and State | Tensile Strength | Yield Strength | Rate of Elongation | Brinell Hardness |
| Rm N/mm2 | RP0.2N/mm2 | A5% | HB | |
| Hastelloy B | ≥760 | ≥350 | ≥40 | - |
| Hastelloy B-2 | ≥760 | ≥350 | ≥40 | - |
| Hastelloy C | 690 | 310 | 40 | - |
| Hastelloy C-4 | ≥690 | ≥276 | ≥40 | - |
| Hastelloy C-22 | ≥690 | ≥310 | ≥45 | - |
| Hastelloy C-276 | ≥690 | ≥283 | ≥40 | - |
| Hastelloy C-2000 | ≥690 | ≥283 | ≥45 | - |
| Hastelloy G-30 | ≥586 | ≥241 | ≥30 | - |
| Hastelloy X | ≥586 | ≥241 | ≥30 | - |
| Hastelloy S | ≥110 | ≥52 | ≥46 | - |