Product Description
PU5110 is a one-component polyurethane adhesive. When exposed to moisture in the air, a chemical reaction occurs and solidifies into a cross-linked elastomer. It has high strength, high elasticity, excellent bonding, impact resistance, water resistance, electrical insulation properties and oil resistance. Widely used in industrial assembly of various substrates.
1. High-strength bonding and sealing of front and rear windshields, side windows, car bodies, ships and other parts of cars and buses.
2. Bonding of glass and car body steel plates, aluminum plates, fiberglass reinforced plastics, and paint surfaces.
- Room temperature cure
- High tensile, shear and tear strength
- Excellent flexibility and impact resistance
- Excellent weather resistance and aging resistance
- Suitable for bonding a variety of materials
Before curing:
| Appearance | Black paste |
| Tack free(min) | 30-60 |
| Cure speed (mm/24hr) | 3.5 |
| Density (g/cm3) | 1.2 |
| Thixotropic stability (sag resistance) | Excellent |
After curing:
| Shear strength (MPa) | 3.8 |
| Tensile strength (MPa) | 6.0 |
| Elongation at break (%) | 380 |
| Hardness (Shore A) | 56 |
| Tear strength (N/mm) | 20 |
Note: Testing and curing are under standard conditions of 23°C, 50%RH.
The product is very sensitive to moisture and therefore needs to be stored in airtight packaging. Store sealed in a cool, dry place, with a shelf life of 6 months at 5-28°C.
310mL; 400mL sausage; 600mL sausage; 25Kg; 240Kg