According to the different application scope, PVC can be divided into: universal PVC resin, high polymerization degree PVC resin, cross-linked PVC resin. General purpose PVC resin is formed by polymerization of vinyl chloride monomer under the action of initiator; High polymerization degree PVC resin refers to the resin which is polymerized by adding chain growth agent in the polymerization system of vinyl chloride monomer; Crosslinked PVC resin is a resin which is polymerized by adding crosslinker containing diene and polyene into vinyl chloride monomer polymerization system.
According to the method of obtaining vinyl chloride monomer, it can be divided into calcium carbide method, ethylene method and imported (EDC, VCM) monomer method (customary ethylene method and imported monomer method are called ethylene method).
According to the polymerization method, PVC can be divided into four categories: suspension polyvinyl chloride, emulsion polyvinyl chloride, bulk polyvinyl chloride and solution polyvinyl chloride. Suspension polyvinyl chloride is the largest variety of production, accounting for about 80% of the total production of PVC. Suspension polyvinyl chloride is divided into six models according to absolute viscosity: XS-1, XS-2... XS-6; XJ-1, XJ-2... , XJ-6. The meaning of each letter in the model: X-suspension method; S-loose type; J-compact type.
According to the plasticizer content, PVC plastic is often divided into: no plasticizer PVC, plasticizer content is 0; Rigid PVC, plasticizer content is less than 10%; Semi-rigid PVC, plasticizer content is 10-30%; Soft PVC, plasticizer content is 30-70%; Polyvinyl chloride paste plastic, plasticizer content of more than 80%
Introduction
Used to produce soft films, sheets, artificial leather, pipes, profiles, corrugated pipes, cable protection tubes, packaging films, shoe soles and various soft sundries.Packing:25KG/BAG , 17MTS without pallet/20GP
25KG/BAG , 27MTS without pallet/40GP
Introduction
Used for films, sheets, artificial leather, wires, cables and various soft profiles, etc.Packing:25KG/BAG , 17.5MTS without pallet/20GP
25KG/BAG , 28MTS without pallet/40GP
Specification
| Product Name | Suspension polyvinyl chloride resin S1300 | Designation | ||
| Standard | Q/SH3160 77-2019 | Batch Number | ||
| Sampling location | 1#Packaging line | Sampling time | ||
| Item | Index | Inspection result | ||
| Superior | Qualified | |||
| Appearance | White powder | White powder | ||
| K-value | 72-70 | 70 | ||
| Average degree of polymerization | 1250-1350 | 1300 | ||
| Apparent density, g/ml | 0.45-0.52 | 0.5 | ||
| Volatile(including water content), % | ≤0.30 | 0.11 | ||
| 100g plasticizer absorption, g | ≥27 | 28.6 | ||
| VCM residue ug/g | ≤2.0 | 0.8 | ||
| Screenings250um sieve pore, % | ≤2.0 | 1.2 | ||
| Screenings63um sieve pore, % | ≥95 | 98 | ||
| Number of "fish eye", /400 cm² | ≤10 | 8 | ||
| Number of Impurity particles | ≤16 | 12 | ||
| Whiteness(160ºC,10min), % | ≥78 | 86.2 | ||
| Dry popular, min | Report value | 0.67 | ||
Storage and transportation
Store in a cool and ventilated warehouse. Keep away from fire and heat source. It should be stored separately from oxidant and avoid mixed storage. Fire fighting equipment of corresponding variety and quantity shall be provided. The storage area should be equipped with suitable materials to contain the leakage.