Product Description
Phenolic Fiberglass Molding Plastics
This series of products are thermosetting molding plastics made of e-glass fiber and modified phenolic resin by soaking and baking. It is used for pressing heat-resistant, moisture-proof, mildew proof, high mechanical strength, good flame retardant insulating parts, but also according to the requirements of the parts, the fiber can be properly combined and arranged, with high tensile strength and bending strength, and suitable for wet conditions.
- Mechanical Excellence: Our composite material boasts excellent mechanical properties, ensuring durability and reliability in various applications.
- Electrical Insulation: With superior electrical insulation, our product provides a safe and reliable solution for electrical components and systems.
- Arc Resistance and Anti-Static: Designed to resist arcs and prevent static electricity, our composite material ensures enhanced safety and performance.
- Corrosion Resistance: Our product exhibits remarkable resistance to corrosion, making it suitable for use in environments with acid, alkali solutions, and other chemicals.
- Lightweight and High Product Utilization: Thanks to its lightweight nature, our composite material offers ease of use and high product utilization, maximizing efficiency and reducing costs.
- Strong Designability: Our composite material allows for versatile design options, enabling creative and innovative solutions in various industries.
- Wide Range of Applications: With its exceptional properties, our composite material finds extensive use across different industries, providing reliable solutions for diverse needs.
| NO. | Test Items | Unit | Index | Test |
| 1 | Resin Content | % | Customized | 38.6 |
| 2 | Volatile Matter Content | % | 3.0-6.0 | 3.87 |
| 3 | Density | g/cm3 | 1.65-1.85 | 1.9 |
| 4 | Water Absorption | mg | ≤20 | 15.1 |
| 5 | Martin Temperature | ºC | ≥280 | 290 |
| 6 | Bending Strength | MPa | ≥160 | 300 |
| 7 | Impact Strength | KJ/m2 | ≥50 | 130 |
| 8 | Tensile Strength | MPa | ≥80 | 180 |
| 9 | Surface Resistivity | Ω | ≥10x10^11 | 10x10^11 |
| 10 | Volume Resistivity | Ω.m | ≥10x10^11 | 10x10^11 |
| 11 | Medium wearing factor (1MHZ) | - | ≤0.04 | 0.03 |
| 12 | Relative Permittivity (1MHZ) | - | ≥7 | 11 |
| 13 | Dielectric Strength | MV/m | ≥14.0 | 15 |
It is suitable for pressing mechanical components with high strength, electrical components with complex shape, radio parts, mechanical parts and electrical parts with high strength and commutator (commutator), etc. Its products also have good electrical performance, especially suitable for hot and humid areas.
It should be stored in a dry and ventilated room where the temperature does not exceed 30ºC.
Do not close to fire, heating and direct sunlight, erect stored on a special platform, horizontal stacking and heavy pressure are strictly prohibited.
Shelf life is two months from the date of production. After the storage period, the product can still be used after passing the inspection according to the product standards. Technical standard: JB/T5822-2015