Audited Supplier
Mflam TC100
68333-79-9
REACH, RoHS
Yes
White
Plastic Flame Retardant
Powder
PP and Glass Fiber Reinforced PP
UL94 V0
About 280 Degrees Celsius
Less Than 190 Degrees Celsius
Mflam
25kg/Bag, 20mt/20'fcl
Ammonium Polyphosphate
China
2835399000
Product Description
Phosphorus and Nitrogen Based Flame Retardant Powder for Polyolefins Reach UL 94 V-0 at 1.6mm
Specification:
| Item | Index |
| Appearance | White Powder |
| The Content of Phosphorus %(W/W) | 25±2 |
| The Content of Nitrogen %(W/W) | 20±2 |
| Particle Size D50 (μm) D90 (um) | 9±3 23±4 |
| TGA (20ºC/min, in N2) | Weight Loss 1%:≥220ºC |
| Weight Loss 5%: ≥290ºC | |
| Recommend Process Condition ºC | ≤ 190 |
| Moisture %(W/W) | ≤0.5 |
Application:
Mflam TC100 is a halogen-free intumescent flame retardant designed by our company for polyolefins with phosphorus and nitrogen as the main flame retardant elements; it mainly plays a flame retardant role in the formation of carbon and expansion flame retardant. It has high flame retardant efficiency, good thermal stability, no precipitation, good water resistance, light aging resistance and low smoke and non-toxicity. PP treated by Mflam TC100 (adding 25%-28%) can reach UL 94 V-0 (1.6mm). Mflam TC100 can also be used in glass fiber reinforced PP, and can reach UL 94 V-0 (0.8mm).
Recommended dosage in plastic:
| Polymer | PP | PP+GF (10%) | PP+GF (20%) | PP+GF (30%) | PP+talcum powder (20%) |
| Mflam TC100 dosage % | 25-30 | ≥25 | ≥25 | ≥25 | 24-26 |
| Flame Retardancy | V-0(1.6mm) | V-0(1.6mm) | V-0(0.8mm) | V-0(1.6mm) | V-0(3.2mm) |
| Polymer | PE | ||
| Mflam TC100 dosage % | Cannot do | 33-36 | 30-32 |
| Flame Retardancy | V-0(0.8mm) | V-0(1.6mm) | V-0(3.2mm) |
Shipping Information:
The package is 25kg craft paper bag or on customer's request, and can be loaded 20mt with pallet in 1x 20'FCL.
Remarks:
(1) The initial thermal decomposition temperature of Mflam TC100 in air is about 280 °C, so the processing temperature of the twin-screw can be adjusted according to the specific conditions to enhance the dispersion and enhance the plasticization effect. A certain degree of hollowness must be maintained during the twin-screw extrusion process.
(2) When Mlam TC100 is used in PP, it is not recommended to use a combination of strong shear screws.