Product Description
Product Description
Dipped tire cord fabric
It is mainly made of nylon 6,nylon 66 and polyester, has advantage as:
1. high breaking strength,
2. excellent impact resistance,
3. high fatigue-proof strength,
4. good adhesive strength with rubber.
It is the high quality skeleton material of various rubber products
which take the important role that insures shape and bears load.
Feature
High breaking strength,
High anti-fatigue strength,
Excellent impact resistance,
Good bearing performance,
Good adhesive strength with rubber.
Usage
It is widely used in the reinforcement for
rubber tire,
conveyor belts,
rubber hoses,
flexible oil tanks for military purpose.
Packing and delivery:
1. Packing details : International standard export packing in packages or according to customer's requirement.
The fabric is wound on a wooden shaft / iron shaft, then wrapped with black polyethylene film, and then covered by PE film, finally tightly PP woven bag.
Every roll weight/length according to customer's requirement.
2. Payment Terms : 100% L/C at sight or 30% T/T in advance, 70% at sight of B/L copy.
3. Delivery Time :
after received workable deposit
2 -5 days for samples
15-20 days for 1-3 20 fcl containers
20-30 days for 3-5 20 fcl containers
4. Sample:
Free supply.
Express Cost more than 15 USD, please tell me account No. of DHL,TNT, EMS etc, We do freight collect.
Company Profile:
HL Group Ltd is the manufacturer and exporter of tire and rubber hose framework materials for the industrial sector in global market.
It has been professionals in the framework materials for 20 years.
The products covers:
tyre cord fabric for tyre and fishing net,
EE/EP/NN fabric for conveyor belt,
Liner fabric for tyre,
Filter fabric for
Various industries,
bead wire for tyre and hose,
steel cord for tyre,
rubberized tyre cord fabric for tyre and hose,
rubberized steel cord for tyre and hose.
Products are sold to all large tire factory in China and also export to Southeast Asia, Africa, Europe, South America so on.
Our group insist on quality first, customer focus, win-win policy.
Sincerely hope to cooperate with you.
Specification:
Nylon 6 Dipped Tyre Cord Fabric Specification
Polyester Dipped Tire Cord Fabric STD Specification
Polyester Dipped Tyre Cord Fabric HMLS Specification
Product pictures:
Why choose us?
1.A professional international sales team, which is specialized in the framework materials for 16 years.
2.Well and high-quality control
3. Strong production capacity and testing capabilities
4.Various designs are available
5.Prompt delivery
6.FREE SAMPLE can be offered
Dipped tire cord fabric
It is mainly made of nylon 6,nylon 66 and polyester, has advantage as:
1. high breaking strength,
2. excellent impact resistance,
3. high fatigue-proof strength,
4. good adhesive strength with rubber.
It is the high quality skeleton material of various rubber products
which take the important role that insures shape and bears load.
Feature
High breaking strength,
High anti-fatigue strength,
Excellent impact resistance,
Good bearing performance,
Good adhesive strength with rubber.
Usage
It is widely used in the reinforcement for
rubber tire,
conveyor belts,
rubber hoses,
flexible oil tanks for military purpose.
Packing and delivery:
1. Packing details : International standard export packing in packages or according to customer's requirement.
The fabric is wound on a wooden shaft / iron shaft, then wrapped with black polyethylene film, and then covered by PE film, finally tightly PP woven bag.
Every roll weight/length according to customer's requirement.
2. Payment Terms : 100% L/C at sight or 30% T/T in advance, 70% at sight of B/L copy.
3. Delivery Time :
after received workable deposit
2 -5 days for samples
15-20 days for 1-3 20 fcl containers
20-30 days for 3-5 20 fcl containers
4. Sample:
Free supply.
Express Cost more than 15 USD, please tell me account No. of DHL,TNT, EMS etc, We do freight collect.
Company Profile:
HL Group Ltd is the manufacturer and exporter of tire and rubber hose framework materials for the industrial sector in global market.
It has been professionals in the framework materials for 20 years.
The products covers:
tyre cord fabric for tyre and fishing net,
EE/EP/NN fabric for conveyor belt,
Liner fabric for tyre,
Filter fabric for
Various industries,
bead wire for tyre and hose,
steel cord for tyre,
rubberized tyre cord fabric for tyre and hose,
rubberized steel cord for tyre and hose.
Products are sold to all large tire factory in China and also export to Southeast Asia, Africa, Europe, South America so on.
Our group insist on quality first, customer focus, win-win policy.
Sincerely hope to cooperate with you.
Specification:
Nylon 6 Dipped Tyre Cord Fabric Specification
| Item | 1870dtex/2 (1680D/2) | 1400dtex/2 1260D/2 | 930dtex/2 840D/2 | 2100dtex/2 (1890d/2) | 1170dtex/1 (1050D/1) | 700dtex/1 (630D/1) | 1870dtex/1 (1680D/1) | 1400dtex/1 (1260D/1) | 930dtex/1 (840D/1) | ||
| Breaking strength≥ | N/end | 279.30 | 215.60 | 137.20 | 313.60 | 90.00 | 50.00 | 137.00 | 107.00 | 70.00 | |
| Elongation at | 88.2N | % | 9.5±0.5 | - | - | 9.5±0.5 | - | - | 8.0±0.8 | - | - |
| 66.6N | - | 9.5±0.5 | - | - | 8.0±0.8 | - | - | 7.0±0.8 | - | ||
| 44.1N | - | - | 9.5±0.5 | - | - | 7.5±0.8 | - | - | 7.5±0.8 | ||
| Adhesive strength≥ | N/cm | 166.60 | 147.00 | 117.60 | 176.40 | 65.00 | 43.00 | 83.00 | 69.00 | 54.00 | |
| Breaking strength difference≤ | % | 3.80 | 3.80 | 3.80 | 3.80 | 5.00 | 5.00 | 5.00 | 5.00 | 5.00 | |
| Breaking elongation difference≤ | 6.30 | 6.30 | 6.30 | 6.30 | 7.00 | 7.50 | 7.00 | 7.00 | 7.00 | ||
| Dip pick up | 4.5±1.0 | 4.5±1.0 | 4.5±1.0 | 4.5±1.00 | 4.2±0.8 | 4.2±1.00 | 4.2±1.00 | 4.2±1.00 | 4.2±1.00 | ||
| Breaking elongation | % | 23.0±2.0 | 23.0±2.0 | 22.0±2.0 | 23±2.0 | 20.0±2.0 | 19.0±2.0 | 20.0±2.0 | 20.0±2.0 | 20.0±2.0 | |
| Diameter | mm | 0.78±0.03 | 0.65±0.03 | 0.55±0.03 | 0.78±0.03 | - | 0.23±0.03 | 0.5±0.03 | 0.43±0.03 | 0.32±0.03 | |
| Twist | Primary twist(Z) | Twist/m | 320±15 | 370±15 | 460±15 | 320±15 | TPM/m: 200±15 | TPM/m: 260±15 | 160±10 | 190±10 | 210±15 |
| Second twist(S) | 320±15 | 370±15 | 460±15 | 320±15 | |||||||
| Heat shrinkage ≤ | % | 6.00 | 6.00 | 6.00 | 4.00 | 4.50 | 4.00 | 4.00 | 4.00 | 4.00 | |
| Moisture ≤ | % | 1.00 | 1.00 | 1.00 | 1.00 | 0.80 | 0.80 | 0.80 | 0.80 | 0.80 | |
| NO. | ITEMS | UNITE | 1000D/2 | 1300D/2 | 1000D/3 | 1500D/2 | 2000D/2 | 1300D/3 | 1500D/3 | |
| (1100dtex/2) | (1440dtex/2) | (1100dtex/3) | (1670dtex/2) | (2200dtex/2) | (1440dtex/3) | (1670dtex/3) | ||||
| 1 | Breaking Stength (min) | N/end | 140 | 180 | 205 | 205 | 280 | 260 | 305 | |
| 2 | Elongation at 44.1N | % | 4.5+1.0 | |||||||
| Elongation at 58.0N | % | 4.5+1.0 | ||||||||
| Elongation at 66.6N | % | 4.5+1.0 | 4.5+1.0 | |||||||
| Elongation at 88.2N | % | 4.5+1.0 | 4.5+1.0 | |||||||
| Elongation at 100N | % | 4.5+1.0 | ||||||||
| 3 | Adhension(H-test)(min) | N/Cm | 125 | 135 | 140 | 140 | 170 | 165 | 180 | |
| 4 | Breaking strength difference(max) | % | 4 | 4 | 4 | 4 | 4 | 4 | 4 | |
| 5 | Breaking elongation difference(max) | % | 5 | 5 | 5 | 5 | 5 | 5 | 5 | |
| 6 | Dip pick up | % | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | |
| 7 | Breaking elongation (Min.) | % | 15+/-2 | 15+/-2 | 15+/-2 | 15+/-2 | 15+/-2 | 15+/-2 | 15+/-2 | |
| 8 | Diameter | mm | 0.56+0.03 | 0.61+0.03 | 0.66+0.03 | 0.66+0.03 | 0.75+0.03 | 0.74+0.03 | 0.81+0.03 | |
| 9 | Twist | Pingle twist(Z) | T/10cm | 45+1.5 | 40+1.5 | 37+1.5 | 37+1.5 | 33+1.5 | 33+1.5 | 31+1.5 |
| Ply twist(S) | 45+1.5 | 40+1.5 | 37+1.5 | 37+1.5 | 33+1.5 | 33+1.5 | 31+1.5 | |||
| 10 | Hot air shrinkage 177ºC×2minx0.05CN/dtex(max) | % | 3 | 3 | 3 | 3 | 3 | 3 | 3 | |
| 11 | Elongation @ Breaking of weft yarn (Min) | % | 120 | 120 | 120 | 120 | 120 | 120 | 120 | |
| NO. | ITEMS | UNITE | 1000D/2 | 1300D/2 | 1000D/3 | 1500D/2 | 2000D/2 | 1300D/3 | 1500D/3 | |
| (1100dtex/2) | (1440dtex/2) | (1100dtex/3) | (1670dtex/2) | (2200dtex/2) | (1440dtex/3) | (1670dtex/3) | ||||
| 1 | Breaking Stength (min) | N/end | 140 | 180 | 205 | 205 | 270 | 260 | 305 | |
| 2 | Elongation at 44.1N | % | 4.5+1.0 | |||||||
| Elongation at 58.0N | 4.5+1.0 | |||||||||
| Elongation at 66.6N | 4.5+1.0 | 4.5+1.0 | ||||||||
| Elongation at 88.2N | % | 4.5+1.0 | 4.5+1.0 | |||||||
| Elongation at 100N | % | 4.5+1.0 | ||||||||
| 3 | Adhension(H-test)(min) | N/Cm | 125 | 135 | 140 | 140 | 170 | 165 | 180 | |
| 4 | Breaking strength difference(max) | % | 4 | 4 | 4 | 4 | 4 | 4 | 4 | |
| 5 | Breaking elongation difference(max) | % | 5 | 5 | 5 | 5 | 5 | 5 | 5 | |
| 6 | Dip pick up | % | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | |
| 7 | Breaking elongation (min) | % | 14 | 14 | 14 | 14 | 14 | 14 | 14 | |
| 8 | Diameter | mm | 0.56+0.03 | 0.61+0.03 | 0.66+0.03 | 0.66+0.03 | 0.75+0.03 | 0.74+0.03 | 0.81+0.03 | |
| 9 | Twist | Pingle twist(Z) | T/10cm | 45+1.5 | 40+1.5 | 37+1.5 | 37+1.5 | 33+1.5 | 33+1.5 | 30+1.5 |
| Ply twist(S) | 45+1.5 | 40+1.5 | 37+1.5 | 37+1.5 | 33+1.5 | 33+1.5 | 30+1.5 | |||
| 10 | Hot air shrinkage 177ºC×2minx0.05CN/dtex(max) | % | 2 | 2 | 2 | 2 | 2 | 2 | 2 | |
| 11 | Elongation @ Breaking of weft yarn (Min) | % | 120 | 120 | 120 | 120 | 120 | 120 | 120 | |
Why choose us?
1.A professional international sales team, which is specialized in the framework materials for 16 years.
2.Well and high-quality control
3. Strong production capacity and testing capabilities
4.Various designs are available
5.Prompt delivery
6.FREE SAMPLE can be offered