Product Description
Mainly used in the production of various long and short polypropylene fibers, used in the production of polypropylene woven bags, packaging bags, injection molding products and other flame retardant parts used in the production of electrical appliances, telecommunications, lighting, lighting equipment and TV sets, as well as automotive parts part
TDS
Physical properties of | The test conditions | The test method | The test results | unit |
Density/specific gravity | ASTM D792 | 0.898 | G /cm sharp | |
Melt flow rate (melt flow rate) | 230°C/2.16 kg | ASTM D1238 | 3 | g/10 min |
Shrinkage rate - flow | 23°C | Internal methods | 1.4 to 1.8 | % |
Mechanical properties of | The test conditions | The test method | The test results | unit |
Tensile strength | The yield, 23 ° C | ASTM D638 | 25 | Mpa |
elongation | Fracture, 23 ° C | ASTM D638 | > 200 | % |
Bending modulus | 23°C | ASTM D790A | 1080 | Mpa |
Thermal performance | The test conditions | The test method | The test results | unit |
Thermal deformation temperature under load | 1.8mpa, unannealed, 6.35mm | ASTM D648 | 110 | °C |
Impact properties | The test conditions | The test method | The test results | unit |
Notched impact strength of cantilevered beam | -20°C, 3.18 mm | ASTM D256 | 93 | J/m |
23°C, 3.18 mm | ASTM D256 | 590 | J/m |
The injection | The test conditions | The test method | The test results | unit |
Processing (melt) temperature | From 180 to 230 | °C | ||
Mold temperature | 30 to 50 | °C | ||
Injection pressure | 2.94 - 5.88 | Mpa | ||
hardness | The test conditions | The test method | The test results | unit |
Rockwell hardness | R , 23°C | ASTM D785 | 80 | |
flammability | The test conditions | The test method | The test results | unit |
UL flame retardant rating | UL 94 | HB |