1. Introduction:
TZP Milling Media is made from Yttria partially stabilized zirconia, and available for any kinds of mills such as micro mill, ultromicro mill, vibratory mill and ball mill to grind and disperse the material effectively and economically. Characterized with high density and toughness, super hardness, excellent Wear and corrosion resistance, the TZP milling media is regarded as an most attractive material in many applications include: electronic slurry, ceramic powder, magnetic material, battery material, rare-earth material, nonmetal ore, painting, dye, ink, calcium, titanium, pesticide, food stuff and medicine etc. Superior grinding efficiency and minimizing product contamination from media wear are most valued.
2. Main Properties:
Type-1: High Density
| Constituents (%) | ZrO2 Y2O3 | 94.6 5.25 |
| Density | g/cm³ | 6.05 |
| Open Porosity | % | 0 |
| Hardness Vickers | Hv | 1250 |
| E modulus | Gpa | 200 |
| Bending strength (4-point) | MPa | 1300 |
| Fracture strength | MPa*m1/2 | 8 |
| CTE(20~4000C) | *10-6/ K | 9.6 |
Type-2: Low Density
| Constituents (%) | ZrO2 Y2O3 | 94.6 5.25 |
| Density | g/cm³ | 5.80 |
| Hardness Vickers | Hv | 1100 |
| E modulus | Gpa | 200 |
| Bending strength (4-point) | MPa | 900 |
| Fracture strength | MPa*m1/2 | >6 |
Ball: OD0.6mm, OD0.8mm, OD1.0mm, OD1.2mm, OD1.4mm, OD1.6mm, OD1.8mm, OD2.0mm, OD2.2mm, OD2.6mm, OD3.0mm, OD4.5mm, OD5.0mm, OD6.5mm, OD7.0mm, OD8.5mm, OD10.0mm, OD12.0mm, OD15.0mm, OD20.0mm, OD25.0mm, OD30.0mm, OD35.0mm.
Cylinder: OD5mm*Height5mm, OD7*H7, OD10*H10, OD12.7*12.7, OD15*H15, OD20*H20