Pure White High Performance D 30mm Polychlorotrifluoroethylene PCTFE Rod

Price	$600.00 Compare
Min Order	1 kg
Availability	In Stock
Shipping From	Zhejiang, China
Popularity	288 people viewed
Quantity	+-

Ningbo Mbh Engineering Plastic Co., Ltd.

Audited Supplier 3 years

Profile Certified by SGS/BV

Zhejiang, China
Dengfeng Zhou (Mr.)

Visit Homepage Product Catalog

Product Detail
Contact Supplier

Model NO.:

MBH-PCTFED-030

Material:

PCTFE

Kind:

Hard Plastic Rods

Water Absorption:

＜0.01%

Contraction Percentage:

0.4%~1.4%

Tensile Strength:

81~130MPa

Color:

Nature Beige

Size:

Max 260mm Dia. Per Customized

Machining Service:

Yes

Advantage:

High Performance

Modified Service:

Yes

Application Filed:

Medical / E/E / Semiconductor / Aerospace etc

Trademark:

MBH

Transport Package:

as Per Customer's Request

Specification:

as per customer's request

Origin:

China

HS Code:

3926909090

Product Description

PCTFE is a homopolymer of chlorotrifluoroethylene. PCTFE is melt processible and can be extruded or molded. PCTFE has a number of unique properties. In addition to excellent thermal and chemical stability, it has very low moisture absorption and permeation. It also is highly resistant to cold flow, is very rigid, is tough, has excellent dimensional stability and extremely good low temperature properties. It is especially applicable as a valve component material in cryogenic fluid service.

PCTFE Main Advantage:

Especially suitable for cryogenic applications
Excellent resistance to creep
Dimensionally stable over a wide temperature range
Extremely low gas permeability
FDA approval
Transparent and coloured compounds
Working temperature from -240°C to +180˚C

PCTFE - Poly (chloro trifluoro ethylene) TYPICAL PROPERTIES

PCTFE - Poly (chloro trifluoro ethylene) TYPICAL PROPERTIES

Property	Value	Units	Method
MECHANICAL PROPERTIES
Tensile Strength	4860 - 5710 34 - 39	psi MPa	D 638
Elongation	100 - 250	%	D 638
Flexural Strength, 73°F	9570 - 10300 66 - 71	psi MPa
Flex Modulus	200 - 243 x 103 1.4 - 1.7	psi MPa
Impact Strength, Izod, 23 deg C	2.5 - 3.5	ft-lb/in	D 256
Compressive Stress at 1% deformation,	1570 - 1860 11 - 13	psi MPa	D 695
Density	2.10 to 2.17	gm/cu.cm
THERMAL PROPERTIES
Coefficient of Linear Expansion	7 x 10-5	K-1
Melting Point	410 -414 210 - 212	deg F deg C
Thermal Conductivity	1.45 0.84	Btu·in/h·ft2·°F W/m·K	ASTM C 177
Specific Heat	0.22 0.92	Btu/lb/deg F kJ/Kg/deg K
Heat Distortion Temperature, 66 lb/sq.in (0.455 MPa)	259 126	deg F deg C	D 648
Processing Temperature	620 327	deg F deg C
ELECTRICAL PROPERTIES
Dielectric Strength, short time, 0.004"	3000	Volt/mil	D 149
Arc-Resistance	360	sec	D 495
Volume Resistivity, @ 50% RH	2 x 1017	ohm-cm	D 257
Surface Resistivity, @ 100% RH	1 x 1015	Ohm sq-1	D 257
Dielectric Constant, 1 kHz	2.6	ε	D150-81
Dissipation Factor, @ 1 kHz	0.02		D150-81
OTHER PROPERTIES
Water Absorption	0.00	% increase in weight	D570-81
Flame Rating+	Non-flammable		D 635
Coefficient of friction			D 1894
Specific Gravity	2.10 to 2.17		D792
Moisture Permeability Constant	0.2	g/m, 24 hours
O2 Permeability	1.5 x 10-10	Cc, cm/sq.cm, sec, atm
N2 Permeability	0.18 x 10-10	Cc, cm/sq.cm, sec, atm
CO2 Permeability	2.9 x 10-10	Cc, cm/sq.cm, sec, atm
H2 Permeability	56.4 x 10-10	Cc, cm/sq.cm, sec, atm

+ Numerical rating for flame spread is not intended to reflect hazards presented by this or any other material under actual fire conditions