About PVC Compounds:
Cable PVC compounds are thermoplastic materials derived from processing polyvinylchloride compositions, produced as granules. Various properties are imparted to compounds depending on applications and item operation conditions. This is achieved by using plasticizers, stabilizers and modifiers in various combinations in compositions.
PVC based plasticizers have considerable mechanical strength and water resistance, high thermal resistance to low temperatures, good insulation properties, insoluble in gasoline and kerosene, abrasion, acid and alkali resistant. PVC based compounds are readily welded and glued.
Cable PVC compounds are use in the cable and conductor industry for manufacture of insulation and protective wire and cable sheaths. The main final consumers of the PVC based cable and conductor products are energy and construction industries.
Product Name:
- 70 ºC PVC Cable Compound
- 90 ºC PVC Cable Compound
- 105 ºC PVC Cable Compound
- 105 ºC Irradiated crosslinked FR PVC Compound
- 80 ºC Irradiated crosslinked FR PVC Compound
- PVC Compound for Plug
PVC compound can be used for power cables, communication cables, wires, sound lines, video lines, microphones, data cables, charging cables and other cables. Package is normal bag (25kg) or jumbo bag (1000kg).
Technical Data Sheet:
1.Technical specifications of 70 ºC pvc compound
| Tensile strength | MPa | 20.5 |
| Fracture tensile strain | % | 320 |
| Ageing temperature | ºC | 100 |
| Ageing time | h | 168 |
| Tensile strength after ageing | MPa | 22.5 |
| Max change of tensile strength | % | +12 |
| After ageing fracture tensile strain | % | 290 |
| Max change of fracture tensile strain | % | -10 |
| Thermal deformation | % | 28 |
| Thermal ageing quality loss | g/m2 | 19 |
| 200ºC thermal stability time | min | 90 |
| 20ºC volume resistivity | Ω.cm | 2.0*1011 |
2. Technical specifications of 90 ºC pvc resin compound
| Tensile strength | MPa | 20 |
| Fracture tensile strain | % | 330 |
| Ageing temperature | ºC | 100 |
| Ageing time | h | 240 |
| Tensile strength after ageing | MPa | 21.5 |
| Max change of tensile strength | % | +8 |
| After ageing fracture tensile strain | % | 310 |
| Max change of fracture tensile strain | % | -6 |
| Thermal deformation | % | 28 |
| Thermal ageing quality loss | g/m2 | 9 |
| 200ºC thermal stability time | min | 120 |
| 20ºC volume resistivity | Ω.cm | 2.0*1010 |
About us:
Jiangxi Longtai New Material Co., Ltd, founded in 2002, was successfully listed the New OTC Market in 2016, stock code: 836898. Longtai is specialized in the development and sales of all kinds of new materials, wire&cable materials and ariculture products. It has passed ISO9001:2008. All product meet RoHS and REACH by SGS. More than 30% of products are exported to Europe, America, Janpan, Southeast Asia and Africa, and so on.
Main Product:
Cable materials: HF FR PP filler,Submarine cable PP yarn, PP filler,PP tape, PVC/TPE compound etc
Agriculture twines: Tomato twine, Banana twine, Hay baler twine,garden twine etc
Textile materials: Cotton yarn, Polyester yarn, multifilament yarn, PP Fibrillated yarn, PP Flat yarn etc
Package ropes: 2ply rope, 3ply rope, Raffia, Strings etc