- Uniform texture, double-layer filter material structure, layered filtration;
- Stable chemical and physical properties and strong corrosion resistance;
- High filtration efficiency and low resistance;
- Large specific surface area and high dust capacity;
- High hydrophobicity, excellent water and moisture resistance;
- Large expansion strength and high filter material stiffness;
- The fluctuation of banner quantitative and vertical quantitative is very small;
- High temperature resistance, can be used in high temperature environment within 300 ºC.
It is the raw material for the production of diaphragm filter, non diaphragm filter, combined filter and high-efficiency HEPA filter.
| Main components | Superfine glass fiber | Temperature resistance | ≤300ºC |
Filter Grade | F6-U15 | Temp short peaks | 350ºC |
Flame retardant grade | A(GB/T 17591-2006) | Moisture resistance (relative humidity) | ≤100% |
Model | Filtration Class | EFF. | Ration (g/m2) | Thickness (mm) | I.N.P (Pa) | Longitudinal tensile Strength(MD) | Transverse tensile strength(CD) | Water resistancein (h20) | Stiffness (mg) | Combustion loss |
RT-HGF06 | M6 | ≥35% | 70±2 | 0.45±0.06 | ≤20Pa | ≥0.8 | ≥0.65 | ≥15 | ≥900 | 4.5±1.5 |
RT-HGF07 | F7 | ≥50% | 70±2 | 0.45±0.06 | ≤32Pa | ≥1.2 | ≥0.65 | ≥15 | ≥900 | 4.5±1.5 |
RT-HGF08 | F8 | ≥65% | 70±2 | 0.45±0.06 | ≤45Pa | ≥1.3 | ≥0.65 | ≥15 | ≥900 | 4.5±1.5 |
RT-HGF09 | F9 | ≥85% | 70±2 | 0.45±0.06 | ≤70Pa | ≥1.3 | ≥0.65 | ≥15 | ≥900 | 4.5±1.5 |
RT-HGF10 | H10 | ≥95% | 72±2 | 0.4±0.06 | ≤125Pa | ≥1.3 | ≥0.65 | ≥15 | ≥1200 | 4.5±1.5 |
RT-HGF11 | H11 | ≥98% | 72±2 | 0.4±0.06 | ≤180Pa | ≥1.3 | ≥0.65 | ≥15 | ≥1200 | 4.5±1.5 |
RT-HGF12 | H12 | ≥99.8% | 72±2 | 0.4±0.06 | ≤246Pa | ≥1.3 | ≥0.65 | ≥15 | ≥1200 | 4.5±1.5 |
RT-HGF13 | H13 | ≥99.97% | 74±2 | 0.4±0.06 | ≤292Pa | ≥1.3 | ≥0.55 | ≥20 | ≥1200 | 4.5±1.5 |
RT-HGF14 | H14 | ≥99.997% | 74±2 | 0.4±0.06 | ≤370Pa | ≥1.3 | ≥0.55 | ≥20 | ≥1200 | 4.5±1.5 |
RT-HGF15 | U15 | ≥99.9995% | 76±3 | 0.4±0.07 | ≤405Pa | ≥1.3 | ≥0.55 | ≥20 | ≥1200 | 4.5±1.5 |