1100dtex/3
Rubber Hose ; Tyre ; Conveyor Belt
1.283 GSM
Polyester /Nylon with Rubber
Plain
Fabric with Rubber Form
Rubber Coated
Tyre Cord Fabric, Rubberized
as Costomer's Requirement
Our Factory Produced This Product for More Than 10
Now We Have Around 10 Costomers Use This Product
Around 25 Days for 1*20 FCL
LC; Tt
1.0-1.1mm
HL GROUP LTD.
in Rolls
as requirement's requirement
China
5902101000
Product Description
Rubberized tire cord fabrics
Rubberized tire cord fabric is used the high quality fabric calendered by natural rubber, with the characteristics of high tensile strength, black and bright color , smooth surface, stronger adhesion, and longer service time.
There are different thickness of rubberized tire cord fabrics produced by our factory. If you have special requirements, please tell us what products you make, the detailed specifications and the thickness . We can also produce according to your requirements.
Rubberized tyre cord fabric is semi-product of tires, and also can be used to produce rubber hose, tire . Natural rubber calendered fabric is suitable for various rubber products and plays the role of skeleton support.
Characteristics:
Widely used in tire, rubber hose, sole, sand pipe, rubber joint, triangle belt and other rubber products; And also used in oil field pipeline, valve pipeline, Marine pipe fittings, large-caliber oil pipeline, etc.
Specifications:
Nylon 6: 930dtex/2, 1400dtex/2, 1870dtex/2, 2100dtex/2, 1400dtex/3 etc.
Polyester: 1100dex/2, 1100dex/3, 1440dtex/2, 1440dtex/3, 1670dtex/2, 1670dtex/3, 2200dtex/2, 2200dtex/3 etc.
SPECIFICATION OF POLYESTER TIRE CORD FABRIC:
SPECIFICATION OF NYLON TIRE CORD FABRIC:
Note: The above are general technical specifications, which can be adjusted according to customer' requirements.
.
Packing and delivery:
1. Packing details : International standard export packing in packages or according to customer's requirement.
The fabric is wound on a wooden shaft / iron shaft, then wrapped with black polyethylene film, and then covered by PE film, finally tightly PP woven bag.
Every roll weight/length according to customer's requirement.
2. Payment Terms : 100% L/C at sight or 30% T/T in advance, 70% at sight of B/L copy.
3. Delivery Time :
after received workable deposit
2 -5 days for samples
15-20 days for 1-3 20 fcl containers
20-30 days for 3-5 20 fcl containers
4. Sample:
Free supply.
Express Cost more than 15 USD, please tell me account No. of DHL,TNT, EMS etc, We do freight collect.
Why choose us?
1.A professional international sales team, which is specialized in the framework materials for 16 years.
2.Well and high-quality control
3. Strong production capacity and testing capabilities
4.Various designs are available
5.Prompt delivery
6.FREE SAMPLE can be offered
THE PICTURE OF OUR PRODUCT:
The following is the picture of our product, please kindly check:
Welcome to contact with us if your need the product or the similar product.
Rubberized tire cord fabric is used the high quality fabric calendered by natural rubber, with the characteristics of high tensile strength, black and bright color , smooth surface, stronger adhesion, and longer service time.
There are different thickness of rubberized tire cord fabrics produced by our factory. If you have special requirements, please tell us what products you make, the detailed specifications and the thickness . We can also produce according to your requirements.
Rubberized tyre cord fabric is semi-product of tires, and also can be used to produce rubber hose, tire . Natural rubber calendered fabric is suitable for various rubber products and plays the role of skeleton support.
Characteristics:
- high tensile strength
- black and bright color
- smooth surface
- stronger adhesion
- longer service time
Widely used in tire, rubber hose, sole, sand pipe, rubber joint, triangle belt and other rubber products; And also used in oil field pipeline, valve pipeline, Marine pipe fittings, large-caliber oil pipeline, etc.
Specifications:
Nylon 6: 930dtex/2, 1400dtex/2, 1870dtex/2, 2100dtex/2, 1400dtex/3 etc.
Polyester: 1100dex/2, 1100dex/3, 1440dtex/2, 1440dtex/3, 1670dtex/2, 1670dtex/3, 2200dtex/2, 2200dtex/3 etc.
SPECIFICATION OF POLYESTER TIRE CORD FABRIC:
| No. | Item | Unit | 1870dtex/2 (1680D/2) | 1400dtex/2 (1260D/2) | 930dtex/2 (840D/2) | 2100dtex/2 (1890d/2) | 1170dtex/1 (1050D/1) | 700dtex/1 (630D/1) | 1870dtex/1 (1680D/1) | 1400dtex/1 (1260D/1) | 930dtex/1 (840D/1) |
| 1 | Breaking strength (min) | N/end | 279.3 | 215.6 | 137.2 | 313.6 | 90 | 50 | 137 | 107 | 70 |
| 2 | Elongation at 88.2N | % | 9.5±0.5 | - | - | 9.5±0.5 | - | - | 8.0±0.8 | - | - |
| Elongation at 66.6N | % | - | 9.5±0.5 | - | - | 8.0±0.8 | - | - | 7.0±0.8 | - | |
| Elongation at 44.1N | % | - | - | 9.5±0.5 | - | - | 7.5±0.8 | - | - | 7.5±0.8 | |
| 3 | Adhesive strength (min) | N/cm | 166.6 | 147 | 117.6 | 176.4 | 65 | 43 | 83 | 69 | 54 |
| 4 | Breaking strength difference (max) | % | 3.8 | 3.8 | 3.8 | 3.8 | 5 | 5 | 5 | 5 | 5 |
| 5 | Breaking elongation difference (max) | 6.3 | 6.3 | 6.3 | 6.3 | 7 | 7.5 | 7 | 7 | 7 | |
| 6 | Dip pick up | 4.5±1.0 | 4.5±1.0 | 4.5±1.0 | 4.5±1.00 | 4.2±0.8 | 4.2±1.00 | 4.2±1.00 | 4.2±1.00 | 4.2±1.00 | |
| 7 | Breaking elongation difference (max) | % | 23.0±2.0 | 23.0±2.0 | 22.0±2.0 | 23±2.0 | 20.0±2.0 | 19.0±2.0 | 20.0±2.0 | 20.0±2.0 | 20.0±2.0 |
| 8 | Diameter | mm | 0.78±0.03 | 0.65±0.03 | 0.55±0.03 | 0.78±0.03 | - | 0.23±0.03 | 0.5±0.03 | 0.43±0.03 | 0.32±0.03 |
| 9 | Primary twist(Z) | T/10cm | 32±15 | 37±15 | 46±15 | 32±15 | TPM/m: 20±15 | TPM/m: 26±15 | 16±10 | 19±10 | 21±15 |
| Second twist(S) | 32±15 | 37±15 | 46±15 | 32±15 | |||||||
| 10 | Heat shrinkage (max) | % | 6 | 6 | 6 | 4 | 4.5 | 4 | 4 | 4 | 4 |
| 11 | Moisture (max) | % | 1 | 1 | 1 | 1 | 0.8 | 0.8 | 0.8 | 0.8 | 0.8 |
SPECIFICATION OF NYLON TIRE CORD FABRIC:
| No. | Item | Unit | 1870dtex/2 (1680D/2) | 1400dtex/2 (1260D/2) | 930dtex/2 (840D/2) | 2100dtex/2 (1890d/2) | 1170dtex/1 (1050D/1) | 700dtex/1 (630D/1) | 1870dtex/1 (1680D/1) | 1400dtex/1 (1260D/1) | 930dtex/1 (840D/1) |
| 1 | Breaking strength (min) | N/end | 279.3 | 215.6 | 137.2 | 313.6 | 90 | 50 | 137 | 107 | 70 |
| 2 | Elongation at 88.2N | % | 9.5±0.5 | - | - | 9.5±0.5 | - | - | 8.0±0.8 | - | - |
| Elongation at 66.6N | % | - | 9.5±0.5 | - | - | 8.0±0.8 | - | - | 7.0±0.8 | - | |
| Elongation at 44.1N | % | - | - | 9.5±0.5 | - | - | 7.5±0.8 | - | - | 7.5±0.8 | |
| 3 | Adhesive strength (min) | N/cm | 166.6 | 147 | 117.6 | 176.4 | 65 | 43 | 83 | 69 | 54 |
| 4 | Breaking strength difference (max) | % | 3.8 | 3.8 | 3.8 | 3.8 | 5 | 5 | 5 | 5 | 5 |
| 5 | Breaking elongation difference (max) | 6.3 | 6.3 | 6.3 | 6.3 | 7 | 7.5 | 7 | 7 | 7 | |
| 6 | Dip pick up | 4.5±1.0 | 4.5±1.0 | 4.5±1.0 | 4.5±1.00 | 4.2±0.8 | 4.2±1.00 | 4.2±1.00 | 4.2±1.00 | 4.2±1.00 | |
| 7 | Breaking elongation difference (max) | % | 23.0±2.0 | 23.0±2.0 | 22.0±2.0 | 23±2.0 | 20.0±2.0 | 19.0±2.0 | 20.0±2.0 | 20.0±2.0 | 20.0±2.0 |
| 8 | Diameter | mm | 0.78±0.03 | 0.65±0.03 | 0.55±0.03 | 0.78±0.03 | - | 0.23±0.03 | 0.5±0.03 | 0.43±0.03 | 0.32±0.03 |
| 9 | Primary twist(Z) | T/10cm | 32±15 | 37±15 | 46±15 | 32±15 | TPM/m: 20±15 | TPM/m: 26±15 | 16±10 | 19±10 | 21±15 |
| Second twist(S) | 32±15 | 37±15 | 46±15 | 32±15 | |||||||
| 10 | Heat shrinkage (max) | % | 6 | 6 | 6 | 4 | 4.5 | 4 | 4 | 4 | 4 |
| 11 | Moisture (max) | % | 1 | 1 | 1 | 1 | 0.8 | 0.8 | 0.8 | 0.8 | 0.8 |
Note: The above are general technical specifications, which can be adjusted according to customer' requirements.
.
Packing and delivery:
1. Packing details : International standard export packing in packages or according to customer's requirement.
The fabric is wound on a wooden shaft / iron shaft, then wrapped with black polyethylene film, and then covered by PE film, finally tightly PP woven bag.
Every roll weight/length according to customer's requirement.
2. Payment Terms : 100% L/C at sight or 30% T/T in advance, 70% at sight of B/L copy.
3. Delivery Time :
after received workable deposit
2 -5 days for samples
15-20 days for 1-3 20 fcl containers
20-30 days for 3-5 20 fcl containers
4. Sample:
Free supply.
Express Cost more than 15 USD, please tell me account No. of DHL,TNT, EMS etc, We do freight collect.
Why choose us?
1.A professional international sales team, which is specialized in the framework materials for 16 years.
2.Well and high-quality control
3. Strong production capacity and testing capabilities
4.Various designs are available
5.Prompt delivery
6.FREE SAMPLE can be offered