AISI 1215 /SUM23 Free Cutting Steel Round Bar
AISI 1215 FREE CUTTING STEEL BARS,
AISI 1215 COLD DRAWN STEEL ROUND BAR
AISI 1215 COLD DRAWN STEEL SQUARE BAR
AISI 1215 COLD DRAWN STEEL HEXAGONAL BAR
AISI 1215 Low Carbon Free Cutting Steel, bright drawn or smooth turned with a high and consistent level of machinability but limited strength and ductility.
1.Equivalent grades to AISI 1215
2.Chemical Composition of AISI 1215
3.Mechanical propertiers of AISI 1215
4.Sizes and shapes of cold drawn steel bar 1215
5.MOQ: 1ton
6.Delivery time : 7-30 days after order confirmation
7.Payment terms: T/T or L/ C
(1)30% paid by T/T and rest 70% by T/T upon the copy of B/B.
(2)100% irrevocable L/C at sight
8.Mark: including steel material, heat No., pieces, weight, date and so on.
9.Standard packing : surface oiled+plastic firm+anti-water woven cloth
10.Know us more:
Q: Are you manufacturer or trading company ?
A: We have factory producing cold drawn steel bar for more than 20 years. we can supply cold drawn steel bars in round , square, hex and special profiles.
Q: What's your sample policy ?
A: Our sample is free, but customer may need to pay the express cost.
Q: What's your MOQ ?
A: The MOQ is 1ton per size.
Q: What's your delivery time?
A: Generally, our delivery time is 15-20 days after deposit received, we can adjust our production if your order is urgent.
Q: What's your payment term:
A: Usually, if amount is less than 1000usd, we suggest payment through west union , if amount above 1000usd, we suggest TT or LC.
AISI 1215 FREE CUTTING STEEL BARS,
AISI 1215 COLD DRAWN STEEL ROUND BAR
AISI 1215 COLD DRAWN STEEL SQUARE BAR
AISI 1215 COLD DRAWN STEEL HEXAGONAL BAR
AISI 1215 Low Carbon Free Cutting Steel, bright drawn or smooth turned with a high and consistent level of machinability but limited strength and ductility.
1.Equivalent grades to AISI 1215
| AS 1443-1994 | 1214 |
| BS 970-3-1991 | 230M07 |
| EN 10277 | 1.0715 11SMn 30 |
| JIS G 4804 | SUM22 or SUM23 |
| SAE & UNS | 1215 & G12150 |
2.Chemical Composition of AISI 1215
| Chemical composition: | C | Si | Mn | P | S |
| (typical analysis at Saarstahl in %) | 0,08 | <0,05 | 1,00 | 0,07 | 0,30 |
3.Mechanical propertiers of AISI 1215
| Finish | Yield Strength MPa | Tensile Strength MPa | Elongation | Hardness HB |
| % | ||||
| Bright Drawn | 290 - 550 | 400 - 650 | 7 min | 115 - 200 |
| Smooth Turned | 230 - 310 | 370 - 500 | 17 min | 100 - 150 |
4.Sizes and shapes of cold drawn steel bar 1215
| Shapes | Sizes | Processing |
| Steel Round Bar | 5mm to 63.5mm | Cold Drawn |
| Steel Round Bar | 63.5mm-120mm | smooth-turned and polished. |
| cold drawn steel square bar | 5*5mm to 120*120mm | Cold Drawn |
| cold drawn steel hex bar | 5mm to 120mm | Cold Drawn |
| cold drawn steel hexagonal bar | 5mm to 120mm(side to side) | Cold Drawn |
5.MOQ: 1ton
6.Delivery time : 7-30 days after order confirmation
7.Payment terms: T/T or L/ C
(1)30% paid by T/T and rest 70% by T/T upon the copy of B/B.
(2)100% irrevocable L/C at sight
8.Mark: including steel material, heat No., pieces, weight, date and so on.
9.Standard packing : surface oiled+plastic firm+anti-water woven cloth
10.Know us more:
Q: Are you manufacturer or trading company ?
A: We have factory producing cold drawn steel bar for more than 20 years. we can supply cold drawn steel bars in round , square, hex and special profiles.
Q: What's your sample policy ?
A: Our sample is free, but customer may need to pay the express cost.
Q: What's your MOQ ?
A: The MOQ is 1ton per size.
Q: What's your delivery time?
A: Generally, our delivery time is 15-20 days after deposit received, we can adjust our production if your order is urgent.
Q: What's your payment term:
A: Usually, if amount is less than 1000usd, we suggest payment through west union , if amount above 1000usd, we suggest TT or LC.