Product Description
BK-884 is an organoclay (tetraallkyl ammonium bentonite) for solvent-based systems of low to medium polarity.
1. Advantages:
☆ High gelling efficiency over low to medium polarity organic liquids,especially in aliphatic and aromatic solvent and the compound of above.
☆ Easy of incorporation. No need for polar activator or making pregel.
☆ Consistent in rheology and thixotropy development.
☆ Excellent sag resistance and control of viscosity.
☆ Produce gel with light color and high transparency.
☆ Can be added at any step,even can be used in post-addition to correct the final viscosity of a certain batch.
2. Typical Properties:
3. Typical Applications:
4. Incorporations:
BK-884 belongs to the unconventional type of organoclays group, being an easy-to-disperse, self-activated organoclay, BK-884 does not require a chemical (polar) activator to reach the proper level of delamination of the organoclay platelet stacks.
BK-884 can be added at any point in the manufacturing process. If addition is made with polar activator or after grinding, better performance can be expected.
5. Recommended Levels:
The amount of BK-884 rheology modifier required depends upon the type of organic system and the degree of thickening or other properties desired. Addition levels are typically between 0.2%-2.0% based on the total formulation weight.
6. International Countertypes: Bentone®SD-1, Claytone®HY/AF, TIXOGEL® EZ-100.
1. Advantages:
☆ High gelling efficiency over low to medium polarity organic liquids,especially in aliphatic and aromatic solvent and the compound of above.
☆ Easy of incorporation. No need for polar activator or making pregel.
☆ Consistent in rheology and thixotropy development.
☆ Excellent sag resistance and control of viscosity.
☆ Produce gel with light color and high transparency.
☆ Can be added at any step,even can be used in post-addition to correct the final viscosity of a certain batch.
2. Typical Properties:
| Color | Appearance | Density | Moisture (@105ºC,2hrs) | Fineness through 200 mesh | Loss on Ignition ( @1000ºC ) |
| Light White | Free Flowing Powder | 1.65g/cm3 | ≤3.5% | ≥98% | ≤35% |
3. Typical Applications:
| Acrylic paint | Wooden paint |
| Adhesive | Varnish |
| Alkyd paint | Inks(Mineral oil) |
| Anti-corrosion paint | Inks(Nitro) |
| Chlorinated rubber paint | Nitro lacuquer |
| Primer paint | Sealant |
| Polyester paint | Lubricating grease |
| Road paint | Cosmetics |
| Silica paint |
4. Incorporations:
BK-884 belongs to the unconventional type of organoclays group, being an easy-to-disperse, self-activated organoclay, BK-884 does not require a chemical (polar) activator to reach the proper level of delamination of the organoclay platelet stacks.
BK-884 can be added at any point in the manufacturing process. If addition is made with polar activator or after grinding, better performance can be expected.
5. Recommended Levels:
The amount of BK-884 rheology modifier required depends upon the type of organic system and the degree of thickening or other properties desired. Addition levels are typically between 0.2%-2.0% based on the total formulation weight.
6. International Countertypes: Bentone®SD-1, Claytone®HY/AF, TIXOGEL® EZ-100.