This is the embossed silicone rubber with high strength and easy to use .Our product is eco-friendy product , can contact with skin.
Silicone Rubber For Apparel Label TCS-1310C
Features & Usage:
TCS-1310C is an additional liquid silicone rubber with two components. It showed up good characteristics, such as excellent weatherability, dimensional stability, high transparency, avirulent environmental protection, high-adhesive strength, heatproof temperature exceeds 250C. It is widely used in printing of textile.
Technical parameters:
| Items | Data | |
| Before curing | appearance(silicone/curing) | subtransparent/colorless viscous liquid |
| viscosity(silicone/curing)/mPa.s | 300000/500 | |
| Operation time(25ºC)/h | 5 | |
| After curing | hardness/Shore A | 43 |
| density/g.cm-3 | 1.10 | |
| Tensile strength/MPa | 9.0 | |
| elongation/% | 450 | |
| Tear strength/kN.m-1 | 20 | |
| Shrinkage/% | 0.1 | |
Usage:
1.Mixture: Mix up silicone TCS-1310C with curing agent according ratio 10:1. (If curing agent increased, the curing speed will get slower). Mixture can complete by hand or by equipment.
Package, storage & Notes:
- Silicone package: 20KG/pail. Curing gent: 2KG/tin
- Keep it dry, ventilative and cool. To prevent the rain, sun exposure.
- Avoid mixing curing agent of condensation silicone. Below also can influent curing effect, such as amine, sulfur compounds, phosphorus compound & melt salt. Avoiding moisture intrusion in using.
- The products storage period about 1 year. Its fluidity can be recovered when intense agitation. We advised stir the silicone first then stir the silicone & curing agent mixture second. Expired products also can be used if passed re-inspection.
- This products is a non-dangerous goods.
Applycation:
Printing on the back of the fabrics o get 3D embossed effect by heat mold after high frequency embossing machine .
Easy to release from the mold, high transparency, strong adhesion, excellent softness , no fall off after washing , no shape change.
There is no any color migration on PU/Rubber material.
The embossing pattern was lasting and natural on the leatherware which can save long printing effect.
Operation method:
The mix ratio is 10:1
Thinner adding ratio: 10-40%, depends on fabric and embossing process
Heating temperature:150-190 degree
Normally the upside mold with temperature about 190 degree will better and downside mold with tem 150 degree .
Heating time :8-15 seconds ,depends on the heating temperature.