Audited Supplier
Product name:Organic polysilazane IOTA 9108
Product Features
Low viscosity
Short curing time
Various curing methods
High ceramic yield
Good adhesion on the metal \ ceramic \ graphite materials
Easy to prepare SiCN ceramics
High temperature resistance to 1500 ºC
Product description
Organopolysilazane IOTA 9108 is a liquid precursor polymer consisting of repeating Si-N units. It can be used as a thermosetting resin and a ceramic precurs. Under relatively mild conditions, the SiCN ceramic products with good temperature resistance are obtained, especially for high temperature resistant adhesives.
Applications
Ceramic matrix composites (CMCs)
Metal matrix composites
High temperature resistant adhesive
Anticorrosive coating
High temperature resistant anti-oxidation ceramic coating
Ceramic preform impregnated
Thermosetting resin
Organic and inorganic hybrid materials
Packaging:
Upon customer demand, it is packed in 0.5-20 liters in plastic drum, solid content is 99.9%.
Technical Parameters:
| Apparent features: | colorless to light yellow liquid |
| Solid content % | ≥99% (other contents could be customized) |
| Molecular weight (Mn) | 900-1000 |
| Density | 0.98g/cm3-0.99g/cm3 |
| Ceramic density | 1.60-2.00 g/cm-3 |
| Viscosity | 10cp-40cp |
| Cracking threshold | 100µm+(coating thickness) |
Solvent
Polysilazane IOTA 9118 can be diluted with various polar or non-polar dry solvents. It is sensitive to water, alcohol solvents, hydrolysis or alcoholysis reaction, to make the product deteriorate. And it should avoid contact with acid, alkali and other proton type substances.
Curing conditions
IOTA 9108 can be cross-linked under the temperature of 120-180 ° C, curing can be done in air or inert atmosphere.
IOTA 9108 can also do hydrosilylation reaction by platinum catalyst , curing at 80-100 ºC.
The curing time depends on the curing temperature and the amount of catalyst, usually 2-5 h.
Cracking conditions
First, IOTA 9108 cured product converted to amorphous ceramics by high temperature cracking, eventually get crystalline ceramics. It is amorphous product below 1400 ºC, begin to crystallize above 1400 ºC. Ceramic product composition has great relationship with cracking atmosphere, SiC and Si3N4 under nitrogen or argon; mainly Si3N4 under Ammonia; mainly SiOCN under air conditions. In addition, the cured product cracking is easily influenced by filler, and result affects the composition of the final ceramic product.
Shelf life
Shelf life of unopened polysilazane IOTA 9108 is one year; opened polysilazane shelf life is depend on protection measures. Under sealed low temperature drying condition, the lifetime is more than two months.
Clean
Proper cleaning method is important. After use, take acetone or solvent oil immediately to wipe the tool and clean. Once IOTA 9108 cured, the solvent cannot be washed away.
Precautions
When use polysilazane, it should be in a ventilated, dry environment and with the necessary protective measures such as gloves, masks, goggles; We shouldn't put the uncured IOTA 9108 near fire, humid air and water.