Solventless Epoxy Phenolic Coatings Are Used in Water Conservancy and Other Fields

The water tank of the ship is divided into water tank and oil tank, etc. All the coatings on the inner steel plate of the oil tank require good adhesion, mechanical properties, water resistance, oil resistance and other properties. In addition to these properties, the coating also requires the paint film to be clean and non-toxic, and there is no pollution to the water quality it is stored. Before the 1950s, the water tank parts on ships around the world were almost all painted or sprayed with cement slurry walls. But it has been proved by practice that cement is brittle after drying. When it is subjected to shock and vibration, it is easy to crack and spalling. Ship wall steel often less than half a year due to water corrosion and corrosion. The water is polluted. Therefore, beginning in the late 1940s and 1950s, paint was gradually used to replace the method of applying cement slurry, and most of the water tanks of ships were still protected by the paint.
The product is a two-component, high-solid coating with epoxy resin as the main agent. Divided into primer and top paint. Component A is composed of epoxy resin, pigment, additive and auxiliary. Component B is a curing agent formulated with modified amines.

Application field
Good durability, epoxy resin cured paint film tough water resistant, non-toxic film, no pollution to water. Strong adhesion, good adhesion between the paint film and the steel plate, between the paint film and the paint film. Excellent anti-rust and water resistance, the use of excellent anti-rust raw materials, can ensure its anti-rust performance. It has good mechanical strength, tough film, wear resistance and impact resistance. High solid content, thick film. Curing film at room temperature. No need for large baking equipment.
It is widely used in the inner wall coating of water supply facilities such as ship water tank, water pipeline, water tank, water tower and sugar and grain cargo hold. It can also be used as the inner wall coating of swimming pool, cooling tower of power plant and metal and concrete for filling fuel oil and .