YMT2367R
Steel Plate
AISI, DIN, JIS, GB
C: 0.32-0.40 Si:0.30-0.40 Mn:0.30-0.50 V:0.40-0.70
Forged
Block
Black Primer
High-strength Steel Plate, Wear Resistant Steel, Mold Steel
Tool Steel Bar
Aluminum, Zinc, Die Casting and Plastic Mold
YMT
Container or Metal Framework
Max 500mm thickness
China
7224909090
Product Description
YMT2367ESR
YMT2367ESR hot work tool steel has high temperature strength and good wear resistance in high temperature environment, and twice hardened steel has good tempering, high through hardening and toughness, can be used directly during production in cooling water
Chemical Composition :
| Steel grade (%) | C | Si | Mn | Cr | Mo | V |
| YMT 2367ESR | ~0.38 | ~0.40 | ~0.40 | ~5.00 | ~2.5 | ~0.60 |
Main Applications
It is for the production of wear-resistant tools, warm extrusion compression dies, and light and heavy metal forging dies and other hot work tools and accessories. Specially for the higher requirements of working environment, we recommend the use of electroslag remelting steel YMT2367ESR.
Physical Property
Density[g/cm3]:
| 20OC 7.83 |
Thermal Conductivity [W/m.K]:
| 20OC 25 |
Coefficient of Linear Thermal Expansion 10-6°C-1
| 20-100 °C | 20-200 °C | 20-300 °C | 20-400 °C | 20-500 °C | 20-600 °C | 20-700 °C |
| 11.5 | 12.0 | 12.2 | 12.5 | 12.9 | 13.0 | 13.2 |
Non-metallic Inclusion
As per ASTM E45 method A
At ≤1.5, Bt≤l.5, Ct≤l.5, Dt≤l.5; Ad≤1,5, Bd≤l.5, Cd≤1.5, Dd≤l.5 or DIN50602-K4≤20 or subject to customer's requirements.
UT Test Standard
SEP 1921 Group3, Class E/e or subject to customer's requirements.
Delivery Conditions
Delivered in pre-hardened condition, max hardness 235HB, or according to customer's requirement.
Heat-Treatment
Air cooling, oil quenching or 450-550OC salt bath. App. HRC50-56
| Soft annealing temperature | Quenching temperature |
| 800-840OC | 1030-1080OC. Air cool, oil cool or hot bath (500-550OC, Quenching hardness 53-57HRC. |
Stress Relieving
Heat to 650OC, keep in furnace for one hour, then air cooling in order to alleviate stress during machining
Or reduce the deformation caused in the heat treatment.
Tempering and Hardness, UTS
| Tempering temperature [ o C] | 100 | 200 | 300 | 400 | 500 | 550 | 600 | 650 | 700 |
| HRC | 57 | 55 | 54 | 53 | 56 | 56 | 53 | 43 | 31 |
| UTS ([N/mm2 ] | 2140 | 1980 | 1910 | 1845 | 2010 | 2050 | 1845 | 1360 | 995 |