Product Description
Stainless Steel Fitting
Process,:
Cold & Mandrel Forming
Sizes:
Seamless Type: 1/2"-20"(DN15-DN500)
Welded Type: 1/2"-48" (DN15-DN1200)
Standards:
GB/T12459, GB/T13401, SH3408, SH3409, ASME/ANSI B16.9, B16.28, ASTM A403, MSS SP-43, JIS B2311, JIS B2312, JIS B2313
WT Sch5S-Sch80S, Sch10-Sch160, XS-XXS
Materials:
TP304, TP304H, TP304L, TP316, TP316L, TP321, TP321H, TP317L, TP310S, TP347H.
Process,:
Cold & Mandrel Forming
Sizes:
Seamless Type: 1/2"-20"(DN15-DN500)
Welded Type: 1/2"-48" (DN15-DN1200)
Standards:
GB/T12459, GB/T13401, SH3408, SH3409, ASME/ANSI B16.9, B16.28, ASTM A403, MSS SP-43, JIS B2311, JIS B2312, JIS B2313
WT Sch5S-Sch80S, Sch10-Sch160, XS-XXS
Materials:
TP304, TP304H, TP304L, TP316, TP316L, TP321, TP321H, TP317L, TP310S, TP347H.
| Grade | Chemical Composition | Others | Mechanical Properties, min | |||||||||||
| ASTM | Tensile Strength Ksi (Mpa) | Yeild Point Ksi (Mpa) | Elongation % min | Hardness Test Max | ||||||||||
| C | Si. | Mn | P | S | Ni | Cr | Mo | HB | HRB | |||||
| max | max | max | max | max | min | min | min | |||||||
| 304 | 0.08 | 0.75 | 2.00 | 0, 045 | 0.03 | 8.00~11.00 | 18.00~20.00 | - | - | 75(515) | 30(205) | 35 | 192 | 90 |
| 304 L | 0.035 | 0.75 | 2.00 | 0, 045 | 0.03 | 8.00~13.00 | 18.00-20.00 | - | - | 70(485) | 25(170) | 35 | 192 | 90 |
| 309 | 0.15 | 0.75 | 2.00 | 0, 045 | 0.03 | 12.00~15.00 | 22.00~24.00 | - | - | 75(515) | 30(205) | 35 | 192 | 90 |
| 310 | 0.15 | 0.75 | 2.00 | 0, 045 | 0.03 | 19.00~22.00 | 24.00~26.00 | - | - | 75(5150 | 30(205) | 35 | 192 | 90 |
| 316 | 0.08 | 0.75 | 2.00 | 0, 045 | 0.03 | 11.00~14.00 | 16.00~18.00 | 2.00~3.00 | - | 75(515) | 30(205) | 35 | 192 | 90 |
| 316 L | 0.035 | 0.75 | 2.00 | 0, 045 | 0.03 | 10.00~15.00 | 16.00~18.00 | 2.00~3.00 | - | 70(485) | 25(170) | 35 | 192 | 90 |
| 316 Ti | 0.08 | 0.75 | 2.00 | 0, 045 | 0.03 | 11.00~14.00 | 16.00~18.00 | 2.00~3.00 | Ti: 5xC% ~0.75 | 75(515) | 30(205) | 35 | 192 | 90 |
| 317 | 0.08 | 0.75 | 2.00 | 0, 045 | 0.03 | 11.00~14.00 | 18.00~20.00 | 3.00~4.00 | - | 75(515) | 30(205) | 35 | 192 | 90 |
| 321 | 0.08 | 0.75 | 2.00 | 0, 045 | 0.03 | 9.00~13.00 | 17.00~20.00 | - | Ti: 5 x C% ~ 0.70 B | 75(515) | 30(205) | 35 | 192 | 90 |
| 321 H | 0.04~ 0.10 | 0.75 | 2.00 | 0, 045 | 0.03 | 9.00~13.00 | 17.00~20.00 | - | Ti: 4 x C% ~0.60 | 75(515) | 30(205) | 35 | 192 | 90 |
| 347 | 0.08 | 0.75 | 2.00 | 0, 045 | 0.03 | 9.00~13.00 | 17.00~20.00 | - | Nb + Ta: 10 x C% ~1.00 | 75(515) | 30(205) | 35 | 192 | 90 |
| 347 H | 0.04~ 0.10 | 0.75 | 2.00 | 0, 045 | 0.03 | 9.00~13.00 | 17.00~20.00 | - | Nb +Ta: 8 XC% ~ 1.0 | 75(515) | 30(205) | 35 | 192 | 90 |
| 410 | 0.15 | 1.00 | 1.00 | 0, 040 | 0.03 | 0.75 | 11.5~13.5 | - | - | 60(415) | 30(205) | 20 | 207 | 95 |
| 430 | 0.12 | 1.00 | 1.00 | 0, 040 | 0.03 | 0.75 | 16.00~18.00 | - | - | 60(415) | 35(240) | 20 | 190 | 90 |