Product Description
Production Description
1- Product Induction
S-1111 is a self-crosslinking silicon-modified styrene-acrylic emulsion with extremely fine particle size, with excellent comprehensive performance
2-Features
The appearance is transparent and the dry film gloss is excellent
Good leveling, fast drying, easy construction
Good film formation, high gloss retention after dilution, effectively reducing costs
High hardness of paint film, good stain resistance and good blocking resistance
3-Application
The product is mainly used for cost-effective high-gloss top paint for handicrafts
4-Technical Parameter
| Appearance | Milky white translucent liquid |
Solid Content % | 49~50% |
PH(25ºC) | 7.0~9.0 |
Viscosity(NDJ-1,No.3,60rpm,25ºC,mPa·s) | 3000~6000cps |
Minimum film forming temperature (MFT) (ºC) | 26-30ºC |
5-Package &Storage
Package 25KG 50KG 200KG plastic drum and IBC tank.
Storage
1- Acrylic Emulsion should be stored in a dry and ventilated room, avoid direct sunlight, and the storage temperature is 5 to 35 °C.
2- The effective storage period is six months from the date of packaging
3- It is recommended to dilute with deionized water. If you need to add powder, it is better to use non-ionic pigment wetting agent.
About Us
Shandong Kunhan New Material Technology Co., Ltd. was established in 2006 and is located in Linzi District, Zibo City, the ancient capital of Qi State. The company has a registered capital of 10 million yuan and covers an area of 20,000 square meters. It is a comprehensive modern high-tech enterprise integrating R&D, production and sales of water-based acrylic emulsions, water-based nano-coatings and new fluorine-containing materials. There is a set of acrylic emulsion production equipment with an annual production capacity of 50,000 tons, a set of multifunctional monomer equipment with an annual production capacity of 600 tons, and a R&D center. The company has 113 employees, including 32 R&D personnel, and more than 60% of the employees have a college degree or above.