Swipe or use the arrows to view product images.
China Supplier 1.2mm Cuai11fe/Ercuai-A3/Scu6240 Welding Wire
| Price | $12.00 |
|---|---|
| Min Order | 500 kg |
| Availability | In Stock |
| Shipping From | Hunan, China |
| Popularity | 419 people viewed |
Model NO.:
Ercuai-A3
Type:
Rolling Wire
Material:
Copper / Copper Alloy
Flux Containing:
Not Containing Flux
Slag Characteristic:
Acidic
Extended Length:
>20mm
MOQ:
500kg
Samples:
Free Charge
Delivery Time:
15 Days
Package:
15kg
Trademark:
Xunzhuo
Transport Package:
15kg/Spool
Specification:
0.8mm 0.9mm 1.0mm 1.2mm 1.6mm
Origin:
China
HS Code:
8311100000
Product Description
China Supplier 1.2mm Cuai11fe/Ercuai-A3/Scu6240 Welding Wire
Silicon Bronze is a copper based filler metal that contains 3% Silicon and trace amounts of manganese, tin and zinc. It is used primarily for oxyacetylene welding of copper, copper-silicon and copper-zinc metals to themselves and to steel. Silicon Bronze is excellent for plain or galvanized steel sheet metal as well as other coated steels. It is also used for surfacing areas that are subjected to corrosion. The Oxyacetylene gas flame should be slightly oxidizing. Keep the weld puddle small in order to promote fast solidification and minimize cracking. A high boric acid flux should be used both before and during welding. Preheat is NOT recommended.
Silicon Bronze is a copper based filler metal that contains 3% Silicon and trace amounts of manganese, tin and zinc. It is used primarily for oxyacetylene welding of copper, copper-silicon and copper-zinc metals to themselves and to steel. Silicon Bronze is excellent for plain or galvanized steel sheet metal as well as other coated steels. It is also used for surfacing areas that are subjected to corrosion. The Oxyacetylene gas flame should be slightly oxidizing. Keep the weld puddle small in order to promote fast solidification and minimize cracking. A high boric acid flux should be used both before and during welding. Preheat is NOT recommended.
Grade number | The name of the | Meet (comparable) standards | Main Chemical Composition (%) | Features and Uses | |
GB | AWS | ||||
S201 | Special copper welding wire | SCu1898 | ERCu | Sn1 Si0.3 Mn0.3 Cu Rem. | Good mechanical properties, good crack resistance. Copper gas welding and argon arc welding. |
S211 | Silicon bronze welding wire | SCu6560 | ERCuSi-A | Si3 Mn1 Cu Rem. | Good mechanical performance, copper alloy MIG brazing with argon arc welding and steel |
S212 | Phosphor bronze welding wire | SCu5180 | ERCuSn-A | Sn5 Cu Rem. | Good wear resistance. Copper alloy argon arc and steel surfacing |
S213 | Phosphor bronze welding wire | SCu5210 | ERCuSn-C | Sn8 Cu Rem. | Good wear resistance. Copper alloy argon arc and steel surfacing |
S214 | Aluminum bronze welding wire | SCu6100A | ERCuA1-A1 | A17.5 Cu Rem. | Wear and corrosion resistance. Argon arc welding of copper alloy and surfacing of steel |
S215 | Aluminum iron bronze welding wire | SCu6180 | ERCuA1-A2 | A19 Cu Rem. | Wear and corrosion resistance. Argon arc welding of copper alloy and surfacing of steel |
S216 | Aluminum-nickel bronze welding wire | SCu6327 | --- | --- | --- |
Note:
1.Before welding the oxide,oil and other contaminants on the welding edge of the workpiece and welding wire surface must be cleaned,therwise it will lead to porosity, slag and other defects, so that the performance of the weld is reduced.
2.The addition of tin expands the temperature range between the solid and the liquid phase.In order to reduce the thermal tendency in small pool and fast welding is appropriate.
3.T tungsten inert gas arc welding, the workpiece requires preheating,only with the flat position welding