Copper Coated Saw Wires H10mn2 Welding Wire for High Strength Steel Welding
| Price | $820.00 |
|---|---|
| Min Order | 1 Ton |
| Availability | In Stock |
| Shipping From | Anhui, China |
| Popularity | 452 people viewed |
Model NO.:
HH-H10Mn2
Type:
Rolling Wire
Material:
Stainless Steel
Flux Containing:
Not Containing Flux
Slag Characteristic:
Acidic
Extended Length:
>20mm
OEM & ODM:
Accepted
Handover:
Negotiable; Around 30-35 Days
Certificate:
ISO 9001; CE; RoHS; Reach; OHSAS
Annual Production Capacity:
200000 Tons
Trademark:
Honglu
Transport Package:
Negotiable
Specification:
0.8; 1.0; 1.2; 1.6
Origin:
Anhui, China
HS Code:
7505220000
Product Description
| sports event | tensile strength Rm/MPa | yield strength ReL/Rp0.2MPa | elongation A% |
| standard value | 490-670 | >=490 | >=18 |
| example value | 564 | 459 | 29 |
Uses: This top-quality welding wire is ideally suited for the automatic submerged arc welding of carbon steel and low alloy steel, designed to deliver an equivalent corresponding strength level. Perfect for use in demanding sectors such as shipbuilding, petrochemicals, and boiler manufacturing.
Characteristics: Introducing HH-H10Mn2, an exceptional copper-plated, non-alloy submerged arc welding wire. Paired with SJ101 flux, it offers an outstanding welding process performance. You'll appreciate its beautifully shaped weld channels, easy deslagging, and remarkable low-temperature impact toughness.
Chemical Composition of Welding Wire: (Mass Fraction) 100%
| sports event | C | Mn | Si | S | P | Cr | Ni | Cu |
| standard value | <=0.12 | 1.50-1.90 | <=0.07 | <=0.030 | <=0.030 | <=0.20 | <=0.30 | <=0.35 |
| example value | 0.11 | 1.65 | 0.05 | 0.017 | 0.022 | 0.022 | 0.02 | 0.116 |
1. To ensure optimal flux performance, bake it at a temperature range of 250-400 ºC for 1-2 hours. Ensure the welding wire is kept in a dry, oil-free, and rust-free condition before use.
2. Prior to welding, perform telding to thoroughly remove rust, oil, water, and any other impurities.
3. Maintain strict control with sulfur content of flux at <= 0.050% and phosphorus content at <= 0.060%.
- Similar Products
$270000.00
5 Tons (MOQ)
Low Temperature High Strength Welding Wire Er80s-Ni2
Shandong Solid Solder Co., Ltd.
Negotiable
1000 kgs (MOQ)
Best Price Stainless Steel Welding Wire Er316LSI
Hangzhou Linan Dayang Welding Material Co., Ltd.