Cpm S30V Material Powder Metallurgy Stainless Steel Black Surface Forging Steel Hot Rolled Steel Flat Bar Round Bar

Price $46000.00
Min Order 1 Ton
Availability In Stock
Shipping From Hubei, China
Popularity 550 people viewed
Send Inquiry View Full Page
Model NO.:
powder stainless steel
Type:
Special Steel Bar
Standard:
AISI, ASTM, DIN, JIS, GB, BS
Composition:
Stainless Steel Scrap
Technique:
Forged
Shape:
Bar
Surface Treatment:
Polished
Special Use:
High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel
Application:
Die Steel Bar
Length:
2500-5500mm
Material:
HSS
Usage:
Gear Hob
Customized Support:
OEM
Trademark:
Smooth
Transport Package:
N/M
Specification:
6-400mm
Origin:
China
HS Code:
7226911000
Product Description

Detailed Photos

Product Description
 
CPM S30V is a martensitic stainless steel designed to offer the best combination of toughness, wear resistance and corrosion resistance. Its chemistry has been specially balanced to promote the formation of vanadium carbides which are harder and more effective than chromium carbides in providing wear resistance. CPM S30V offers substantial improvement in toughness over other high hardness steels such as 440C and D2, and its corrosion resistance is equal to or better than 440C in various environments. The CPM process produces very homogeneous, high quality steel characterized by superior dimensional stability, grindability, and toughness compared to steels produced by conventional processes.

Typical Applications:
Long-Wearing Specialty Cutlery
Plastic Injection and Extrusion Feed Screws and Dies
Non-Return Valve Components
Pelletizing Equipment
Wear Components for Food and Chemical Processing

Note: These are some typical applications. Your specific application should not be undertaken without independent study and evaluation for suitability.

Chemical Composition:
CPM S30VCarbonChromiumVanadiumMolybdenum
 1.45%14.00%4.00%2.00%
     
Physical Properties:
Elastic Modulus      32 X 106psi       (221 GPa)
Density              0.27 lbs./in3      (7.47 g/cm3)
Thermal Conductivity
BTU/hr-ft-°F     W/m-°K       cal/cm-s-°C
200°F   93°C            10         17.31        4.13 X 10-2

Coefficient of Thermal Expansion

°F            °C           in/in/°F       mm/mm/°C
70 - 400     (20 - 200)     6.1 X10-6    (11.0 X10-6)
70 - 600     (20 - 315)    6.4 X10-6    (11.5 X10-6)

Mechanical Properties:
Toughness (Transverse Charpy C-notch Testing)
GradeImpact Energy
CPM S30V10.0 ft. Lbs.
154 CM2.5 ft. Lbs.
440C2.5 ft.lbs.
Although the longitudinal toughness for all three of these grades is about 25-28 ft. lbs., the transversetoughness of CPMS30V is four times greater than that of 440C or 154CM. These higher transversetoughness results indicate that CPMS30V is much more resistant to chipping and breaking in applications which may encounter side loading. In knifemaking, its higher transverse toughness makes CPM S30V especially good for bigger blades.

Edge Retention (CATRATesting Relative to 440C)
Grade%
CPM S30V145
154CM120
440C100
The CATRA(Cutlery &Allied Trades Research Association) test machine performs a standard cutting operation and measures the number of silica impregnatedcards which are cut (TCC = total cards cut). It is considered a measure of relative wear resistance.
Corrosion Resistance Average Pitting Potential measurements from Polarization Curves run in 5% NaCl (Sodium Chloride) Solution at Room Temperature: (Higher voltage pitting potential indicates better corrosion resistance.)

Thermal Treatments:
Forging: 
2100°F (1150°C) Do not forge below 1750°F (950°C).
Annealing:
Heat to 1650°F (900°C), hold 2 hours, slow cool no faster than 25°F (15°C) per hour to 1100°F (595°C), then furnace cool or cool in still air to room temperature.

Annealed Hardness: About BHN 255

Stress Relieving Annealed Parts: 
Heat to 1100-1300°F (595-705°C), hold 2 hours, then furnace cool or cool in still air.
Hardened Parts: 
Heat to 25-50°F (15-30°C) below original tempering temperature, hold 2 hours, then furnace cool or cool in still air.
Straightening: 
Best done warm 400-800°F (200-430°C)

Hardening
Preheat: 
Heat to 1550-1600°F (845-870°C) Equalize.

Austenitize:
1900-2000°F (1035-1095°C), hold time at temper ature 15-30 minutes.


Quench:
Air or positive pressure quench (2 bar minimum) to below 125°F (50°C), or salt or interrupted oil quench to about 1000°F (540°C), then air cool to below 125°F (50°C).


Temper:
Double temper at 400-750°F (200-400°C). Hold for 2 hours minimum each time. (See Table) A freezing treatment may be used between the first and second tempers. Freezing treatments help to attain maximum hardenability and must always be followed by at least one temper.

NOTE: For optimum stress relieving, CPM S30V may be tem pered at 1000-1025°F (540-550°C). Tempering in this range may result in a slight decrease in corrosion resistance.

Size Change:
+0.05 to +0.10% when fully martensitic. The presence of retained austenite may reduce the net growth. When tempering at 400-750°F (200-400°C), freezing treatments may be necessary to minimize retained austenite.


Recommended Heat Treatment:
Austenitize 1950°F (1065°C). Quench to below 125°F (50°C). Double temper at 600°F (315°C) 2 hrs. minimum each temper. Cool to hand warm between tempers. A freezing treatment may be added between tempers.
Aim hardness: 58-61 HRC.