Enicrmo-3 Nickel Alloy Welding Rod Welding Electrode 2.5-5.0mm
| Price | $5.50 |
|---|---|
| Min Order | 1000 kg |
| Availability | In Stock |
| Shipping From | Zhejiang, China |
| Popularity | 386 people viewed |
Model NO.:
Enicrmo-3
Type:
N (Nickel/Nickel-Alloy Welding Electrode)
Material:
Nickel / Nickel Alloy
Diameter:
2.5mm, 3.2mm, 4.0mm, 5.0mm
Length:
300-450mm
Electrode Coating Type:
Low Hydrogen Sodium
Slag Characteristic:
Acidic
Stainless Steel Welding Rod Type:
Chromium Nickel Stainless Steel
Function:
Surfacing Electrode, Low Hydrogen Type Electrode, Hardfacing Electrode
Welding Power:
DC/AC
Trademark:
TYUE
Transport Package:
5kg/Box, 20kg/Carton
Origin:
China
HS Code:
831110000
Product Description
Heat Temperature Enicrmo-3 Nickel/Nickel Alloy Welding Rods/Electrodes
GB/T 13814 ENi6625
AWS A5.11 ENiCrMo - 3
Feature and use: Ni625 is a low hydrogen type electrode coated nickel base alloy, chemical composition, code-named NiCr22Mo9Nb, adopts dc amphibious, good welding technology, weld metal mechanical properties, and corrosion resistance to high-temperature performance is good, good crack resistance. Used for Inconel625, Incoloy800, Incoloy800H, and Incoloy825 nickel base and iron-nickel base of high-temperature corrosion resistant alloy welding, also can be used for the 9 ni steel and duplex stainless steel welding.
Deposited metal chemical composition (%) :
| C | Mn | Fe | Si | Ni | Cu | |
| Standard Value | ≤0.10 | ≤2.0 | ≤7.0 | ≤0.8 | ≤55.0 | ≤0.5 |
| Typical Value | 0.045 | 0.86 | 3.55 | 0.56 | 61.62 | 0.06 |
| Cr | Nb | Mo | S | P | Other | |
| Standard Value | 20.0~23.0 | 3.0~4.2 | 8.0~10.0 | ≤0.015 | ≤0.020 | ≤0.5 |
| Typical Value | 21.31 | 3.66 | 8.16 | 0.003 | 0.008 | - |
| Yield Strength Rp0.2/MPa | Tensile Strength Rm/MPa | Elongation A/% | |
| Standard Value | ≥420 | ≥760 | ≥27 |
| Typical Value | 435 | 765 | 41 |
Refertotheweldingcurrent(DC+):
| Electrode Diameter /mm | 3.2 | 4.0 |
| Welding Rod Length /mm | 300 | 350 |
| Welding Current/A | 80-100 | 110-150 |
1. Before welding electrode must be approved by 300-350 ºC for 1 hour, which increases with the increasing drying;
2. It must be removed before welding surface rust, oil, water, and other impurities;
3. Must be used when welding short arc operation, narrow welding method.
Our Other Welding Products
If you are interested, please click on the below picture to enter the link
If you are interested, please click on the below picture to enter the link
| Stainless Steel Welding Electrodes | Hardfacing Welding Electrodes | Cast Iron Welding Electrodes |
| Aluminum Welding Wire | Flux Cored Welding Wire | Co2 MIG Welding Wire ER70S-6 |
| FAQ |
Q: What is delivery time / lead time ?
A: 2-3 weeks.
Q: What is your minimum order ?
A: 3000kgs/each size. (MOQ for stainless steel welding electrode)
Q: Can we visit your factory ?
A: Yes. Welcome to visit our factory at any time.
Q: Can you provide free sampe ?
A: Yes. Free samples are available for you.
- Similar Products
$920.00
1 Ton (MOQ)
Welding Rod Welding Electrode Aws A5.1 E6013 E4303
Shandong Solid Solder Co., Ltd.