Liquid Vinyl Unsaturated Polyester Resin for Power Generation Pipeline Steel and Other Fields of Corrosion-Resistance Parts
| Price | $2.40 |
|---|---|
| Min Order | 220 kg |
| Availability | In Stock |
| Shipping From | Shandong, China |
| Popularity | 259 people viewed |
Model NO.:
WL-9001C
Molecular Principal Chain:
Carbon Chain Polymer
Color:
Transparent Yellow
Purity:
99.9%
MOQ:
220 Kg
Warranty:
1
Quality:
High Qulaity
Trademark:
Wanglin
Transport Package:
Metal Drum
Specification:
Synthetic Resin And Plastics, Resin
Origin:
Shandong
HS Code:
3907910000
Product Description
Product Description
WL-9001C is A bisphenol A type epoxy vinyl resin, and the resin has high strength, good heatresistance, wide applicability and other advantages.It can withstand the erosion of most acids, alkalis, salt solutions and some solvents below 100°C.
Application
WL-9001C resin is suitable for hand lay-up, pultrusion, winding and other FRP forming processes, it use to produce corrosion-resistant integral FRP products of various specifications,it also use to produce corrosion-resistant FRP protective layers on the surfaces of metal structures and concrete structures.
Properties
Performance | Parameter | Unit | Standard test |
Appearance | Transparent yellow liquid | - | GB/T8237-2005 |
Viscosity 25ºC | 300-500 | mPa.s | GB/T7193-2008 |
Acid value | 6-14 | MgKOH/g | GB/T2895-2008 |
Solid content | 54-60 | % | GB/T7193-2008 |
Gel time 25ºC | 8-14 | minutes | GB/T7193-2008 |
Note: 25ºC Gel time: 100g resin with 1.0g vinyl accelerator and 1.5g M50 (Akzo-Nobel).
Liquid resin properties(Typical value)
Liquid resin properties(Typical value)
Performance | Date | Unit | Standard test |
Storage Period (Non trigger,darkness),20ºC | 3 | month | - |
Typical properties of resin castings
Performance | Parameter | Unit | Standard test |
Tensile Strength | 75 | Mpa | GB/T2567-2008 |
Tensile modulus of elasticity | 3500 | Mpa | GB/T2567-2008 |
Elongation at break | 3.5 | % | GB/T2567-2008 |
Bending strength | 130 | Mpa | GB/T2567-2008 |
Bending elastic modulus | 3200 | Mpa | GB/T2567-2008 |
Impact strength | 14 | KJ/m2 | GB/T2567-2008 |
Heat distortion temperature | 110 | ºC | GB/T1634-2004 |