Magnesium Stabilized Zirconia Ceramic for Ultra-High Temperature
| Price | $50.00 |
|---|---|
| Min Order | 1 Piece |
| Availability | In Stock |
| Shipping From | Fujian, China |
| Popularity | 400 people viewed |
Application:
Aerospace, Electronics, Medical, Industrial Ceramic
Flexural Strength:
>1000 MPa
Purity:
95%
Type:
Ceramic Parts
Color:
Yellow/White
Density:
4.6-5.6%
Porosity:
1-18.5%
Zro2:
60-95%
Al2O3:
0.2-20%
Sio2:
0.2-1%
MGO:
MGO/Y2o3
Fe2o3:
0.1-0.3%
TiO2:
0.1-1.0%
Application Temperature:
0°c-2200ºC
Applicable Environment:
Air, Vacuum, or Atmosphere Protection Environment
Trademark:
INNOVACERA
Transport Package:
Standard Cartons with Foam
Specification:
Customized
Origin:
Fujian, China
Product Description
Magnesium Stabilized Zirconia Ceramic Tube
Magnesia Stabilized Zirconia (MSZ) is a great refractory and insulating material due to high oxygen ion conductivity, high strength and toughness, and good thermal shock resistance. It has a clean melt at temperatures above 1900°C and above and is specially manufactured for melting superalloys and precious metals. Its superior thermal shock resistance to temperatures reaching up to 2200°C.
Advantages
Advantages
* High thermal shock resistance
* High wear-resistant and erosion-resistant
* Metal corrosion resistance in high temperature
* Excellent non-wetting characteristics
* High strength
* Long service life
* The stabilizers and grains combination can be designed according to customer's using environment.
Application Temperature
0°C-2200
Applicable Environment
Air, Vacuum, or Atmosphere Protection Environment
* High wear-resistant and erosion-resistant
* Metal corrosion resistance in high temperature
* Excellent non-wetting characteristics
* High strength
* Long service life
* The stabilizers and grains combination can be designed according to customer's using environment.
Application Temperature
0°C-2200
Applicable Environment
Air, Vacuum, or Atmosphere Protection Environment
Application Field
High temperature melt flow control
Sizing nozzle, Ladle skateboard panel, Converter slag blocking slide plate and ring, etc.
Specialty glass manufacturing
Large size high content of zirconia and alumina ceramics, etc.
Metal powder industry
Setter plate, Gas atomizing nozzle, etc.
Precious metal smelting industry
Ceramic Crucibles, etc.
Artificial/Laser Crystal Ceramic Temperature Field
Rare earth composite oxide solid solution ceramic temperature field, etc
Sizing nozzle, Ladle skateboard panel, Converter slag blocking slide plate and ring, etc.
Specialty glass manufacturing
Large size high content of zirconia and alumina ceramics, etc.
Metal powder industry
Setter plate, Gas atomizing nozzle, etc.
Precious metal smelting industry
Ceramic Crucibles, etc.
Artificial/Laser Crystal Ceramic Temperature Field
Rare earth composite oxide solid solution ceramic temperature field, etc
Technical Indicators | |||||
Indicators | ltem | Units | MSZ-H | MSZ-L | Custom |
ZrO2 | % | ≥95 | ≥95 | 60-95 | |
AI203 | % | ≤0.2 | ≤0.2 | 0.2-20 | |
SiO2 | % | ≤0.4 | ≤0.4 | 0.2-1 | |
MgO | % | ≤2.9 | ≤2.9 | MgO/Y203 | |
Fe203 | % | ≤0.1 | ≤0.1 | 0.1-0.3 | |
TiO2 | % | ≤0.1 | ≤0.1 | 0.1-1.0 | |
Physical | Color | - | Yellow | Yellow | Yellow/White |
Density | g/cm3 | ≤5.2 | 5.4-5.60 | 4.6-5.6 | |
Porosity | % | ≤18.5 | ≤8 | 1-18.5 | |
The stabilizers, grains combination and porosity can be designed according to customer's using environment. | |||||