Roof Crylic Acid High Elastic Waterprood Coating
| Price | $3.00 |
|---|---|
| Min Order | 4 Tons |
| Availability | In Stock |
| Shipping From | Beijing, China |
| Popularity | 370 people viewed |
Model NO.:
HCA-108
Color:
White
Appearance:
Liquid
Main Raw Material:
Acrylic
Method:
Brush
Level:
Finish Coat
Drying Method:
Air Drying
Certification:
ISO9001
Substrate:
Steel
Components:
Acrylic
Formation Mechanism:
Conversion Type
Package:
20 Kgs/Pail, 36 Pails/ Wooden Case
Trademark:
Yuhong
Transport Package:
barrel
Specification:
Standard Q/SY YHF 014-2005
Origin:
China
HS Code:
32091000
Product Description
Features:
1.100% pure acrylic elastic emulsion is base material.
2. Outstanding outdoor durability and anti-ultraviolet radiation.
3. Outstanding cohesiveness, applicable to steel structure base, cement mortar or concrete base, etc.
4. Durable low-temperature flexibility, crack-free bending under -30 degree low temperature.
5. Excellent elasticity.
6. Environmental water paint, pollution free..
7. Liquid state, cold process, safe and easy.
1.100% pure acrylic elastic emulsion is base material.
2. Outstanding outdoor durability and anti-ultraviolet radiation.
3. Outstanding cohesiveness, applicable to steel structure base, cement mortar or concrete base, etc.
4. Durable low-temperature flexibility, crack-free bending under -30 degree low temperature.
5. Excellent elasticity.
6. Environmental water paint, pollution free..
7. Liquid state, cold process, safe and easy.
| No. | Item | Technical specification | ||||
| 1 | Solid content, % ≥ | 65 | ||||
| 2 | Surface drying time, h ≥ | 4 | ||||
| 3 | Hard drying time, h ≥ | 8 | ||||
| 4 | Low temperature flexibility, °C | -25 | ||||
| 5 | Tensile strength, MPa ≥ | 1.5 | ||||
| 6 | Elongation at break, % ≥ | 300 | ||||
| 7 | Tearing strength, N/mm ≥ | 14 | ||||
| 8 | Penetration | 0.3MPa, 30min watertight | ||||
| 9 | Bond strength, MPa ≥ | 0.5 | ||||
| 10 | Heating expansion rate, % | Prolongation ≤ | 1.0 | |||
| Shortening ≤ | 1.0 | |||||
| 11 | Manual accelerate ageing treatment | Tensile strength maintenance rate, % | 80 ~ 150 | |||
| Rupture prolongation ratio, %≥ | 300 | |||||
| Low temperature flexibility, °C ≥ | -25 | |||||