Stainless Steel Welding Electrodes Aws E308L-16 Welding Rod
| Price | $3.50 |
|---|---|
| Min Order | 1000 kg |
| Availability | In Stock |
| Shipping From | Zhejiang, China |
| Popularity | 478 people viewed |
Model NO.:
E308-16, E308L-16, E309-16, E309L-16
Type:
Stainless Steel Welding Electrodes
Material:
Stainless Steel
Diameter:
2.5mm
Length:
300-400cm
Welding Core Type:
Stainless Steel
Electrode Coating Type:
Titanium Calcium
Slag Characteristic:
Acidic
Stainless Steel Welding Rod Type:
Chromium Stainless Steel
Function:
Low Hydrogen Type Electrode, Gravity Electrode, Moisture-Proof Electrode
Welding Power:
AC/DC
Trademark:
TYUE
Transport Package:
Carton
Specification:
5kgs/inner box, 20kgs/outer carton
Origin:
China
HS Code:
8311100000
Product Description
Product Description
E308L-16 Stainless Steel Welding Electrode/Rod
Description:
A002 is a super-low carbon Cr19Ni10 stainless steel type electrode coated with Titanium-calcium.The molten content is ≤0.04%.It provides excellent performance of intorcry stalline corrosion resistance.It has excellent operational technological performace on both AC and DC.
Application:
It applies to welding the structure of super-low carbon Cr19Ni10 stainless steel.It also suitable for welding the structure of anti-corrosion stainess steel 0Cr19NillT1 which working temperature below 300ºC.It is mainly used for equipment manufacturing of fibre,fertilizer and petroleum industry.
Notes:
1.Electrodes must be baked for 1 hour at 150ºC before welding operation.
2.To operate on DC if all possible.Operate with small current so the electrode will not in red-hot.
3.The anti-corrosion performance and ferrite composition should be detemined between buyer and seller
A002 is a super-low carbon Cr19Ni10 stainless steel type electrode coated with Titanium-calcium.The molten content is ≤0.04%.It provides excellent performance of intorcry stalline corrosion resistance.It has excellent operational technological performace on both AC and DC.
Application:
It applies to welding the structure of super-low carbon Cr19Ni10 stainless steel.It also suitable for welding the structure of anti-corrosion stainess steel 0Cr19NillT1 which working temperature below 300ºC.It is mainly used for equipment manufacturing of fibre,fertilizer and petroleum industry.
| Chemical Composition Deposited Metal (%) | ||||||||
| C | Mn | Si | Cr | Ni | S | P | Mo | Cu |
| ≤0.04 | 0.5~2.5 | ≤0.90 | ≤18~21 | 9~11 | ≤0.03 | ≤0.04 | ≤0.75 | ≤0.75 |
| Mechanical Properties of Deposited metal | ||||||||
| Test Item | Tensile Strength ós (Mpa) | Elongation δ5(%) | ||||||
| Guranteed | ≥520 | ≥35 | ||||||
| Sizes & Recommended Current (AC or DC) | |||||
| Welding rod diameter (mm) | 2.0 | 2.5 | 3.2 | 4.0 | 5.0 |
| welding current (A) | 25~50 | 50~80 | 80~110 | 110~160 | 160~200 |
Notes:
1.Electrodes must be baked for 1 hour at 150ºC before welding operation.
2.To operate on DC if all possible.Operate with small current so the electrode will not in red-hot.
3.The anti-corrosion performance and ferrite composition should be detemined between buyer and seller
-------------------Our Other Welding Products-------------------
If you are interested, please click on the below picture to enter the link
Welding Electrode Carbon Steel, Stainless Steel, Cast Iron etc. | Nickel & Cobalt Based | Flux Cored Welding Wire E71T-1,E71T-1C, E71T-GS,E81T-Ni etc. |
| TIG & MIG Aluminum Welding Wire ER5356,ER4043, ER4047, ER5183 etc. | Submerged Arc Welding Wire EM12,EM12K,EL12,EH14 etc. | Co2 MIG Welding Wire ER70S-6(SG2),SG3 etc. |
- Similar Products
$65.00
5 kilograms (MOQ)
TIG Welding Rods Aws A5.21 Ercocr-B Continous Casting Bare Rods
Shenyang Top New Material Co., Ltd