Two Component Flame Retardant Spray Polyurea Coating
| Price | $5.00 |
|---|---|
| Min Order | 200 kg |
| Availability | In Stock |
| Shipping From | Shanghai, China |
| Popularity | 467 people viewed |
Model NO.:
DIMONDS C1900FR/B2
Color:
Grey
Appearance:
Liquid
Main Raw Material:
Pol/ISO
Method:
Spray
Level:
Finish Coat
Drying Method:
Air Drying
Certification:
ISO14001, ISO9001
Mix Ratio:
1:1.0 (a:B)
Gel Time:
25s
Surface Dry Time:
45s
Tensile Strength:
>10MPa
Elongation at Break:
>300%
Solid Content:
98%
Trademark:
DIMONDS
Transport Package:
Pail/Drum
Specification:
220 kg / barrel for A component; 210 kg / barrel f
Origin:
China
HS Code:
391190
Product Description
Two Component Flame Retardant Spray Polyurea Coating
DIMONDS® C1900FR/B2 flame-retardant spray polyurea is a two-component aromatic polyurea elastomer, which is produced by the reaction of isocyanate component and amino compound component. Professional polyurea spraying equipment is required for construction. In addition to the unique properties of spray polyurea, this product In addition, it is also flame retardant and can meet the DIN4102 B2 standard.
Usage:
Waterproof, anti-corrosion and flame-retardant protection for the surface of various equipment and facilities.
Features :
- Solvent-free, green and environmentally friendly, fast curing.
- Good flame retardant performance.
- Excellent sealing and penetration performance , good impact resistance.
- Dense coating, good flexibility, good impermeability and waterproof performance.
| Item | A component | B component |
| Exterior | light color transparent liquid | color adjustable |
| Specific gravity (g/m³) | 1. 10±0.05 | 1. 10±0.05 |
| Viscosity (cps)@25ºC | 600±300 | 800±300 |
| Solid content (%) | 98 | |
| Mixing ratio ( volume ratio) | 1 | 1 |
| Gel time (s) | 25 | |
| Surface dry time (s) | 45 | |
| Theoretical spreading rate (surface dry film thickness) | 1.2 kg/m2 film thickness 1000 μm | |
Technical Indicators:
| Item | Standard test | Result |
| Tensile strength (Mpa) | GB/T23446-2009 | >10 |
| Elongation(%) | GB/T23446-2009 | >300 |
| Abrasion resistance ( 7 5 0g/500r ) mg | GB/T23446-2009 | <25 |
| Impact strength kg cm | GB/T23446-2009 | ≥50 |
Process Guidance:
- Surface treatment: The surface to be coated must be clean, dry, and free from dust, grease and other impurities.
- Before spraying: Stir component B with an air mixer for at least 15 minutes.
- When spraying, use polyurea special spraying equipment for construction.
Storage conditions:
Storage ambient temperature: 5 - 35 °C.
Packing: 220 kg / barrel for A component; 210 kg / barrel for B component.
The shelf life of the product starts from the date of production and is guaranteed to be in an unopened state.
Part A: 6 months Part B: 6 months.
Make sure the product packaging is sealed.
Store in a cool, ventilated environment, avoid direct sunlight.
Precautions:
1. Before use, component B needs to be fully stirred evenly.
2. It is recommended to use in a well-ventilated environment. In case of accidental contact with skin and eyes, rinse with water immediately.
3. The construction environment temperature should be 5-35°C.
4. During the construction process, keep it clean and dry, and strictly prohibit contact with water, alcohol, acid, alkali, etc.
220 kg / barrel for A component; 210 kg / barrel for B component. 4 drums per pallet.