Wisdom Cual10 Wire Used for Thermal Spray Coating
| Price | $15.00 |
|---|---|
| Min Order | 15 kilograms |
| Availability | In Stock |
| Shipping From | Shanghai, China |
| Popularity | 292 people viewed |
Model NO.:
CuAl10 Wire
Product Type:
Wire
Material:
Cual10 Wire
Carbon Content:
0
PCD:
Semi-Harden
ET:
Cual10 Wire
Hole:
Cual10 Wire
Surface:
Bright
Place of Origin:
Shanghai, China (Mainland)
Brand:
Wisdom
Feature:
Thermal Spray Wire
Name:
Cual10 Wire
Usage:
Coating
Type:
Cu Alloy Wire
Certificate:
ISO9001
Shape:
Wire
Size:
1.6mm
HS Code:
740829
Product Description
Wisdom CuAl10 Wire Used for Thermal Spray Coating
Introduction
CuAl10 is an iron-bearing Copper Aluminium MIG & TIG filler metal primarily designed for
joining aluminium bronze, silicon bronze and manganese bronze, some high strength Copper-Zinc and Copper-Nickel alloys as well as many ferrous metals such as steel,
Cast iron and galvanized iron. It is also good for joining dissimilar metals such as cast iron, carbon steels, copper, bronze and copper-nickel material. Weld deposits exhibit high mechanical ,properties, tensile strength, yield strength and hardness.
SURFACE PREPARATION
Surface should be clean, white metal, with no oxides (rust), dirt, grease, or oil on the surface to be coated. Note: It is best not to handle surfaces after cleaning. Recommended method of preparation is, to grit blast with 24 mesh aluminum oxide, rough grind, or rough machine in a lathe.
Application
Ship constructions
Apparatus
Plumbing
Composition(standard value)%
Typical Physical Properties
Standard Sizes & Packing
Other sizes can be produced by customers' requirement.
Introduction
CuAl10 is an iron-bearing Copper Aluminium MIG & TIG filler metal primarily designed for
joining aluminium bronze, silicon bronze and manganese bronze, some high strength Copper-Zinc and Copper-Nickel alloys as well as many ferrous metals such as steel,
Cast iron and galvanized iron. It is also good for joining dissimilar metals such as cast iron, carbon steels, copper, bronze and copper-nickel material. Weld deposits exhibit high mechanical ,properties, tensile strength, yield strength and hardness.
SURFACE PREPARATION
Surface should be clean, white metal, with no oxides (rust), dirt, grease, or oil on the surface to be coated. Note: It is best not to handle surfaces after cleaning. Recommended method of preparation is, to grit blast with 24 mesh aluminum oxide, rough grind, or rough machine in a lathe.
Application
Ship constructions
Apparatus
Plumbing
Composition(standard value)%
| Standard | Class | Alloy | Cu | Al | Fe | other |
| BS EN14640 | Cu6180 | CuAl10 | Rest | 9.5 | 1 | <0.5 |
Typical Physical Properties
| Solids-Temperature | Density | Elongation | Liquids-Temperature | Tensile Strength | Brinell Hardness |
| 1030°C | 7.6kg/dm³ | 20% | 1090°C | 621N/mm² | 166HB |
Standard Sizes & Packing
| Diameter | Packing | Wire Weight |
| 1/16 (1.6mm) | D 300 Spool | 15kg((33 lb)/spool |