Audited Supplier
Hastelloy C-276
Industrial
JIS, GB, DIN, ASTM
Ni>57%
Alloy
Tube
Not Powder
10~1200mm
Forging
Cold Drawn, Hot Rolled
B575
2.4819
10276
>690MPa
1~2hours(1150-1170degree)
>40%
Ualloy
Standard Seaworthy Package
Thickness 2mm~20mm
China
Product Description
2mm Hastelloy C-276 (W. Nr. 2.4819 ) Sheet Bleach Container Making
Hastelloy C-276 Chemical composition| Alloy | % | Ni | Cr | Mo | Fe | W | Co | C | Mn | Si | V | P | S |
| C | Min. | balance | 14.5 | 15 | 4 | 3 | |||||||
| Max. | 16.5 | 17 | 7 | 4.5 | 2.5 | 0.08 | 1 | 1 | 0.35 | 0.04 | 0.03 | ||
| C276 | Min. | balance | 14.5 | 15 | 4 | 3 | |||||||
| Max. | 16.5 | 17 | 7 | 4.5 | 2.5 | 0.01 | 1 | 0.08 | 0.35 | 0.04 | 0.03 |
Hastelloy C-276 Physical properties
| Density | 8.9 g/cm³ |
| Melting point | 1325-1370 °C |
Hastelloy C-276 Alloy m inimum mechanical properties in the room temperature
| Alloy state | Tensile strength Rm N/mm² | Yield strength R P0. 2N/mm² | Elongation A 5 % |
| C /C276 | 690 | 283 | 40 |
Characteristic as below
1. Excellent corrosion resistance to most of corrosion media in oxidation and reduction environments.
2. Excellent resist pitting, crevice corrosion and stress corrosion cracking performance.
C276 is face-centered cubic lattice structure.
Hastelloy C-276 Corrosion resistance
C276 alloy suit for many kinds of chemical process industry which contain the oxidizing medium and reductant. High molybdenum and chromium content make it can resist the chloride corrosion, and tungsten make it corrosion resistance better.C276 is one of a few material that can resist the corrosion of most chlorine, hypochlorite and chlorine dioxide, this alloy have prominent corrosion resistance to high concentration chlorate( iron chloride and copper chloride).
Hastelloy C-276 Application field
C276 is widely used in the chemical field and petrifaction field, such as the element of chloride organic and catalyze system. This material especially suit for high temperature environment, impure inorganic acid and organic acid (such as formic acid and acetic acid), sea-water corrosion environment.