Detail Information For 50mm Bimetallic Film Blowing Machine Screw and Barrel:
Application: for film blowing extrusion, process recycled HDPE.
Customer's Requirement: good abrasive resistance.
Screw's quality: bimetallic quality, 38CrMoAlA as base steel, 30% tungsten carbide powder will be added in to alloy layer.
Barrel's quality: nitriding quality, 38CrMoAlA as base steel.
Detail Information For All Single Screw and barrel for Extrusion:
Main application: be used in extrusion for film, pipe, recycling, pelleting, sheet, profiles, rod and etc.
Specification:
Diameter: Ø20mm-Ø500mm
L/D ratio: 15-53
Base material :
SKD61
42CrMo
38CrMoAlA(JIS SACM645) from BAOSTEEL company.
Heat treatment:
Advance hardening and tempering
Nitriding treatment
Mid-frequency hardening
Technical Parameters:
Nitriding depth: 0.50mm-0.80mm
Nitriding hardness: HRC56-58
Surface roughness: Ra 0.4
Screw straightness: 0.015mm
Hard chrome layer hardness: HRC58-60
Hard chrome layer thickness: 0.025-0.1mm
Alloy layer depth: 2mm-3mm
Alloy layer hardness: HRC56-64
OULIN SCREW: YOUR LOYAL PARTNER FOR SCREW AND BARREL
COMPANY OVERVIEW:
Application: for film blowing extrusion, process recycled HDPE.
Customer's Requirement: good abrasive resistance.
Screw's quality: bimetallic quality, 38CrMoAlA as base steel, 30% tungsten carbide powder will be added in to alloy layer.
Barrel's quality: nitriding quality, 38CrMoAlA as base steel.
Detail Information For All Single Screw and barrel for Extrusion:
Main application: be used in extrusion for film, pipe, recycling, pelleting, sheet, profiles, rod and etc.
Specification:
Diameter: Ø20mm-Ø500mm
L/D ratio: 15-53
Base material :
SKD61
42CrMo
38CrMoAlA(JIS SACM645) from BAOSTEEL company.
Heat treatment:
Advance hardening and tempering
Nitriding treatment
Mid-frequency hardening
Technical Parameters:
Nitriding depth: 0.50mm-0.80mm
Nitriding hardness: HRC56-58
Surface roughness: Ra 0.4
Screw straightness: 0.015mm
Hard chrome layer hardness: HRC58-60
Hard chrome layer thickness: 0.025-0.1mm
Alloy layer depth: 2mm-3mm
Alloy layer hardness: HRC56-64