ASTM A213 TP304L Sanitary Grade Stainless Steel Pipe
Standard: ASTM SA312
Steel grade: TP304L
Outer diameter: 1"~26"
Wall thickness: 0.8mm~40mm
Length: random length, fixed length
304L stainless steel pipe, its carbon content is lower than material 304, it with same corrosion resistance performance.
After the welding work and stress relieving, 304L material has better intergranular corrosion resistance performance than material 304.
Before the heat treatment, 304L material also keeps very good corrosion resistance.
Operating temperature can be from -196ºCto 800ºC.
Seaworthy packing to protect from damage of surface:
Chemical Composition of 304L stainless steel pipe
Mechanical Properties of 304L stainless steel pipe
Standard: ASTM SA312
Steel grade: TP304L
Outer diameter: 1"~26"
Wall thickness: 0.8mm~40mm
Length: random length, fixed length
304L stainless steel pipe, its carbon content is lower than material 304, it with same corrosion resistance performance.
After the welding work and stress relieving, 304L material has better intergranular corrosion resistance performance than material 304.
Before the heat treatment, 304L material also keeps very good corrosion resistance.
Operating temperature can be from -196ºCto 800ºC.
Seaworthy packing to protect from damage of surface:
Chemical Composition of 304L stainless steel pipe
| Standard | Material | Chemical composition (%) | ||||||
| ASTM A312 | TP 304L | C | Mn | P | S | Si | Ni | Cr |
| ≤0.03 | ≤2.0 | ≤0.035 | ≤0.03 | ≤1.0 | 8.0~11 | 18~20 | ||
| Standard/material | Tensile Strength Mpa | Yield strength Mpa | Elongation % | Hardness | Fusion point ºC |
| ASTM A312 TP304L | ≥520 | ≥205 | ≥40 | HRB<90 HV<200 HBS<187 | 1398~1420 |