Audited Supplier
Mgo 90% min.
Refractory Ramming Mix
Instant Materials
Refractory Ramming Mix
1580< Refractoriness< 1770
Powder
Refractory Material
Ceramic
Lining
Usage
Lining
Ramming Mix
Raw material
Good Mechanical Strength
Low Thermal Conductivity
Good Thermal Insulation Performance
Good Mechanical Strength
Low Thermal Conductivity
Instant Materials
Powdar
Mix
1mt Polybag, 0.5mt Polybag
China
2519909990
Product Description
Ramming Mix For Electric Arc Furnace
Crafted through an advanced synthetic process involving meticulous palletizing and high-temperature burning, this exceptional product ensures the formation of a solid, fully sintered layer when exposed to high temperatures. This premium material is indispensable for expertly ramming the bottoms and slopes of a wide array of electric furnaces, including Ultra High Power (UHP) electric furnaces, High Power (HP) electric furnaces, Regular Power (RP) electric furnaces, Direct Current (DC) electric furnaces, and Open Hearth Furnaces (OHF).
Crafted through an advanced synthetic process involving meticulous palletizing and high-temperature burning, this exceptional product ensures the formation of a solid, fully sintered layer when exposed to high temperatures. This premium material is indispensable for expertly ramming the bottoms and slopes of a wide array of electric furnaces, including Ultra High Power (UHP) electric furnaces, High Power (HP) electric furnaces, Regular Power (RP) electric furnaces, Direct Current (DC) electric furnaces, and Open Hearth Furnaces (OHF).
| Chemical composition and technical performance | Product Brand | ||||||||
| DHL-78 | DHL-83 | ZDL-20 | ZDL-25 | HT70 | |||||
| MgO (%) | ≥ 78 | ≥ 82 | ≥ 81 | ≥ 80 | 63 ~ 69 | ||||
| CaO (%) | 12 ~ 16 | 8 ~ 12 | 11 ~ 14 | 13 ~ 16 | 24 ~ 29 | ||||
| Fe2O3 (%) | 4 ~ 6 | 4 ~ 6 | 3 ~ 5 | 3 ~ 5 | 4 ~ 6 | ||||
| Al2O3 (%) | ≤ 0.6 | ≤ 0.6 | ≤ 0.6 | ≤ 0.6 | ≤ 0.6 | ||||
| SiO2 (%) | ≤ 1.5 | ≤ 1.5 | ≤ 1.2 | ≤ 1.5 | ≤ 1.5 | ||||
| Grain size (mm) | 0 ~ 6 | 0 ~ 6 | 0 ~ 6 | 0 ~ 6 | 0 ~ 6 | ||||
| Strength after burning under the following temperatures | |||||||||
| 1300ºC×3h (MPa) | ≥ 10 | ≥ 10 | ≥ 8 | ≥ 8 | ≥ 8 | ||||
| 1600ºC×3h (MPa) | ≥ 35 | ≥ 35 | ≥ 35 | ≥ 35 | ≥ 35 | ||||
| Linear change rate after burning under the following temperature | |||||||||
| 1300ºC×3h (%) | 0 ~ -0.5 | 0 ~ -0.5 | 0 ~ -0.5 | 0 ~ -0.5 | 0 ~ -0.5 | ||||
| 1600ºC×3h (%) | -1 ~ -3.0 | -1 ~ -3.0 | -1 ~ -3.0 | -1 ~ -3.0 | -1 ~ -3.0 | ||||
| Comprehensive feature | Ceramic | ||||||||