Audited Supplier
Mixed
Mixed
Mixed
Structural Adhesive
Solid-State
Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing
Silicone
Other
Thermosetting Resin
Waterproof
Organic Material
White
Avaliable
24 PCS in a Carton
Installing, Fixing Insulating
ISO 9001: 2008
Global
12 Months
Construction, Woodworking, Sealing Down Pipes
5-10 Min
<1hour
Translucent, White, Black, Aluminum(Grey).
GNS
270ml 280ml 300ml 590ml
China
Product Description
GNS S88 Glass & Metal Silicone Sealant
GNS S88 Glass & Metal Silicone Sealant is a one part neutral cure construction grade silicone sealant that easily extruded in any weather. It cures at room temperature with moisture in the air to produce a durable, flexible silicone rubber seal.
FEATURES
- One part, it can be easily used and extruded with common caulking guns.
- Excellent adhesion to most construction materials without the primmer.
- Outstanding weatherproofing ability, resisting to ultraviolet ray, ozone, snow or temperature extremes.
- Neutral cure, non-acidic, will not corrode metal or other corrosion-sensitive material.
TYPICAL USE
- General glazing and weather sealing in curtain wall and building facades.
- EIFS, the non-structural curtain walls and building construction applications.
- Window e.g.: vinyl windows, doors and perimeter joints.
- Surface like glass, aluminium, ceramics, metals, steel, fiberglass, most plastics, tiles, bricks, marble & granite and so on.
PACKAGING
Available in:
Standard Size:
280ml recyclable plastic cartridge, 24ctgs/ctn
590ml aluminum sausage, 20ssgs/ctn
Special Size:
Contact us for special size.
COLORS
Available for four standard colors: Translucent, White, Black, Grey.
Contact us for special colors.
STORAGE AND SHELF LIFE
12 months from manufacture date when store in cool dry locations below 25ºC, keep away from heat source and direct sunlight during storage.
PERFORMANCE DATA
| Test Parameter | Unit | Result Translucent Pigmented | |
| As Supplied Tested at 23ºC and 50% RH | |||
| Specific Gravity | g/ml | 0.98±0.02 | 1.46±0.02 |
| Flow (sag or slump) | mm | 0 | 0 |
| Extrusion Rate Skin Time | ml/minute minute | 180 5~10 | 102 ≤60 |
| Tack-free Time | hour | ≤1 | ≤5 |
| Curing time (5mm) | hour | ≤12 | ≤16 |
| As Cured-after 21 days at 23ºC and 50% RH | |||
| Durometer Hardness, Shore A | Points | 26 | 42 |
| Elastic Recovery | % | 95 | 94 |
| Movement Capability | % | ±25 | ±20 |
| Tensile/Modulus at 50% Elongation | Mpa | 0.27 | 0.51 |
| Tensile/Modulus at 100% Elongation | Mpa | 0.34 | 0.60 |
| Ultimate Tensile Strength Ultimate Elongation at Break | Mpa % | 0.36 220 | 0.68 420 |