Audited Supplier
Corundum
Strengthen
ISO
High Temperature Resistant
3.85 g/cm3
2.3G/Cm3
700 Hv
59%-62%
26%-29%
9%-12%
Fuda
Barrels
B/Z20: 0.600-0.850mm
China
69149000
Product Description
Ceramic tiles for automotive industry, zirconia Z850, Z600, Z425, Z300, Z210, Z150, Z100
1. Ceramic tablet product description
Ceramic pellets are one of the most commonly used processes to improve metal wear and tear
The surface will significantly improve the fatigue life and mechanical strength of the metal surface.
Ceramic jet has the characteristics of high hardness, high density, low failure rate, good spherical surface, smooth surface, etc,
This is the ideal environment for therapeutic pills. All Zirnano ceramic tablets have passed through six filters and blowdown
At high temperatures, it ensures high purity and can function normally in humid weather.
2. Main characteristics of ceramic fragmentation
High hardness, low penetration rate
The Vickers hardness of ceramic tablets is higher than 700 HV, with low breakdown rate, and can be used for crushing
Processing of gas cylinders made of hard steel, titanium, and aluminum, with high impact energy sprayed onto the metal surface
The points on the metal base will be moved to maintain the integrity of the jet surface and achieve
Smooth and uniform surface;
3.High efficiency and long service life
Ceramic pellets contain 62-66% ZrO2, and their fine structure ensures that they are not easily penetrated
During the shot blasting process, people do not need to frequently refuel new beads, which will save refueling time and
Improve explosion efficiency. Ceramic tablets can be recycled 70-90 times and have reached the end of their service life
Compared to other abrasives, it has a longer service life.
Main technical indicators
Manufacturing Process | ZrO2 | SiO2 | AI2O3 |
59%-62% | 26%-29% | 9%-12% |
Main components:
Level | Main Chemical Index % | ||
ZrO2 | SiO2 | Al2O3 | |
P-B Series(for Sandblasting) | 60-62 | 24-30 | 6-12 |
J-B Series(for Sandblasting) | 62-65 | 24-30 | 4-10 |
Z Series (for shot peening) | 62-65 | 24-30 | 4-10 |
Physical Index | |
True density | 3.85 g/cm3 |
Bulk density | 2.3g/cm3 |
Vicker hardness | 700 HV |
| B/Z20:0.600-0.850mm B/Z 40:0.250-0.425mm B/Z 80:0.125-0.212mm B/Z 120:0.063-0.125mm B/Z 170:0.045-0.090mm | B/Z30:0.425-0.600mm B/Z 60:0.150-0.300mm B/Z 100: 0.106-0.180mm B/Z 150: 0.053-0.106mm B/Z 205:0.000-0.063mm |