Phos-Copper 15 is used for the brazing of copper and copper alloys, brass and bronze.
It can also be used on silver, tungsten and molybdenum.
It is very effective for joining pipe and tubing and is widely used for electrical work.
Phos-Copper 15 should not be used on ferrous metals or copper alloys containing more than 10% nickel because of phosphorous embrittlement due to reactions with iron or nickel.
Of the Phos-Copper brazing filler metals, Phos-Copper 15 has more ductility and better electrical conductivity than the lower silver content Phos-Coppers.
It has good flow and wetting properties on copper, brass and bronze.
Phos-Copper 15 has the most "sluggish" flow characteristics in the PhosCopper family.
This enables it to fill gaps better.
The recommended joint clearances are between 0.001 and 0.005".
Melting of Phos-Copper 15 is virtually complete at 1300°F (704°C) even though the liquidus is not yet reached.
Best results are obtained when brazing slightly above this temperature.
Brazing copper and copper alloys, as well as brass, bronze, silver, tungsten and molybdenum.
Generally, the joint strength produced by Phos-Copper 15 will surpass the strengths of the base metals.
Strength is a function of the base metals being joined, type of joint, design of joint, joint clearances and brazing procedures.
The recommended maximum operating temperatures for Phos-Copper 15 are 300°F (continuous service) and 400°F (intermittent service).
Corrosion resistance is satisfactory except when the joint is in contact with sulfurous atmosphere (especially at elevated temperatures).
The phosphorus at the core of this wire acts as a fluxing agent, and no flux is necessary when brazing copper joints.
However, when used with a copper alloy or one of the other brazeable metals, Silver Flux must be used to promote wetting, bonding, and flow throughout the joint.
The flux used must be active within the required temperature range of Phos-Copper 15 and active throughout the heating cycle.
The flow point of PhosCopper 15 is 1300°F.
| Norms | Ag15P |
| EN1044 | CP102 |
| AWSS5.8 | BcuP-2 |
| DIN8513 | L-Ag15P |
| MELTING POINT | 640-815ºC |
| CHEMICAL COMPOSITION | Ag:15% Cu:80% P:5% |
| SIZE SPECIFICATION | 1.6-5.0mm diameter, 450-1000mm length |
| PACKAGE | 2kg/bag;20kg/carton;500kg/wooden box |
Copper Phosphorus Filler Metals: