Product Description
Copper alloy welding wire Silicon Bronze TIG Welding rod AWS A5.8 ERCuSi-A CuSi3 GTAW for argon arc welding
| CHEMICAL COMPOSITION(%) | |||||||||||||
| Standard | Class | Alloy | Cu | Al | Fe | Mn | Ni | P | Pb | Si | Sn | Zn | Other |
| ISO24373 | Cu6560 | CuSi3Mn1 | bal. | 0.02 | 0.5 | 0.5~ 1.5 | - | 0.05 | 0.02 | 2.8~ 4.0 | 0.2 | 0.4 | 0.5 |
| GB/T9460 | SCu6560 | CuSi3Mn | bal. | max 0.01 | max 0.5 | max 1.5 | - | - | max 0.02 | 2.8~ 4.0 | max 1.0 | max 1.0 | max 0.5 |
| BS EN14640 | Cu6560 | CuSi3Mn1 | bal. | 0.01 | 0.5 | 0.5~ 1.5 | - | 0.02 | 0.02 | 2.8~ 4.0 | 0.2 | 0.2 | 0.4 |
| AWS A5.7 | C65600 | ERCuSi-A | bal. | 0.01 | 0.05 | 1.5 | - | - | 0.02 | 2.8~ 4.0 | 1.0 | 1.0 | 0.50 |
| DIN 1733 | 2.1461 | SG-CuSi3 | bal. | max 0.01 | max 0.3 | 0.5~ 1.5 | - | max 0.02 | max 0.02 | 2.8~ 4.0 | max 0.2 | max 0.2 | max 0.4 |
| TRADE MARK | S211 |
| Equivalent to AWS | ERCuSi-A |
| Characteristics | Good mechanical properties Good corrosion resistance |
| Welding Method | GTAW Argon arc welding |
| Application | Used for TIG,Excellent for plain or coated steels.Also used for sufacing arears subjected to corrossion. |
Best for butt and the hard facing of brass,especially for the MIG welding of zinc coated steel sheet.Pre-heat suggested when MIG hard facing for large size products and use pulsed argon arc welding while hard facing on steel.
| Physical Properties and Mechanical Properties: | |
| Solids-Temperature | 910ºC |
| Liquids-Temperature | 1025ºC |
| Density | 8.5kg/dm3 |
| Tensile Strength | 330-370N/mm2 |
| Elongation | 40% |
| Brinell Hardness | 80-95HB |
| Phosphor Bronze CUSN8P | |||||||||||||
| CHEMICAL COMPOSITION(%) | |||||||||||||
| Standard | Class | Alloy | Cu | Al | Fe | Mn | Ni | P | Pb | Si | Sn | Zn | Other |
| ISO24373 | Cu5210 | CuSn8P | bal. | - | 0.1 | - | 0.2 | 0.01~ 0.4 | 0.02 | - | 7.5~ 8.5 | 0.2 | 0.2 |
| GB/T9460 | SCu5210 | CuSn8P | bal. | - | max 0.1 | - | max 0.2 | 0.01~ 0.4 | max 0.02 | - | 7.5~ 8.5 | max 0.2 | max 0.2 |
| BS EN14640 | Cu5210 | CuSn9P | bal. | - | 0.1 | - | - | 0.01~ 0.4 | 0.02 | - | 7.5~ 9.0 | 0.2 | 0.5 |
| AWS A5.7 | C52100 | ERCuSn-C | bal. | 0.01 | 0.10 | - | - | 0.10~ 0.35 | 0.02 | - | 7.5~ 9.0 | 0.2 | 0.50 |
| Physical Properties and Mechanical Properties: | |||||||||||||
| Solid-Temperature | 875ºC | Liquids-Temperature | 1025ºC | ||||||||||
| Density | 8.8kg/dm3 | Tensile Strength | 260N/mm2 | ||||||||||
| Elongation | 20% | Brinell Hardness | 80HB | ||||||||||
| Introduction: | |||||||||||||
Recommended for the welding of copper with Cu-Sn alloy.Best for the butt joining welding of brass with steel.Pre-heat suggested for the large size Products,and pulsed argon arc welding is recommended for multilayer hard facing on steel. | |||||||||||||
Anhui Hengtai Welding Materials Co., Ltd.which is a professional manufacturer of copper and copper alloy welding materials.Company adopted GB/T9460, BS EN14640, AWS, DIN standards, the production of copper, Silicon Bronze, Aluminum Bronze, Tin Bronze, White Copper, Brass, Copper Base Alloy welding materials, and is widely used in automobiles, ships,engineering machinery, metallurgy, electric power, aviation, aerospace, oil and other fields.Our company has been to Arabia, Dubai, Germany, the United States, France, the Middle East, and Vietnam for many times to conduct academic exchanges.Through years of communication with the majority of users and accumulated experience, the company provides each customer with high-quality, reliable copper alloy series welding materials and thoughtful and detailed pre-sale and after-sales service, "integrity-based, win-win cooperation" is the company's corporate culture and purpose, we will cast a common dream with the spirit of craftsmen.
Our products are suitable for automobile casting, high pressure valve iron, hydraulic rod, marine casting, aerospace casting,ocean exploration, precision machinery, deep sea scale, marine water scale, high pressure valve, etc. Our company is a world leader in the field of copper alloys, and has made outstanding contributions to the field of copper alloy welding in the world.Our company has been to Arabia, Dubai, Germany, the United States, France, the Middle East, and Vietnam for many times to conduct academic exchanges and promote the world. Development in the field of copper alloy welding.