Thermoplastic Polyolefin (TPO) roofing membranes are a popular choice in the construction industry for single-ply roofing systems due to their exceptional performance and durability. Produced using state-of-the-art AMUT facilities sourced from Italy, these TPO membranes are of the highest quality, meeting rigorous international standards.
The product has obtained CE and FM certifications, ensuring compliance with European and international safety and performance requirements. Notably, the TPO membrane boasts an artificial climate-accelerated aging time of 15,000 hours, significantly surpassing the national standard. This remarkable feature enhances the membrane's aging resistance, waterproofing capabilities, thermal insulation properties, and wind uplift resistance, making it a superior choice for various roofing applications.
CANLON, a leading manufacturer in the industry, stands out by producing both type G and GL TPO and PVC waterproof membranes. Their products exhibit clear competitive advantages over peers, particularly in dimensional stability, weather resistance, and wind uplift resistance, making them a preferred choice for high-performance roofing solutions.
Canlon TPO membrane is available within three categories:
- H(stands for non-reinforced smooth one).
- L (stands for fiber fleece-backed one)
- P(stands for Polyester Reinforced one)
- G(stands for Glassfibre Reinforced one)
- GL(stands for Glassfibre Reinforced with Fleece Backing one)
| Thickness(mm) | Width(m) | Length(m) | Color choice |
| 1.2 | 2.0 | 20 | white |
| 2.0 | 2.0 | 15 | |
| 2.5 | 2.0 | 10 | |
| Remarks | Warranty: 10-20 years Other sizes or colors are designed based on requirements | ||
Application
Canlon TPO membrane is mainly applicable to vehicle, paper making, tobacco, textile printing, and IT industry, especially applied in new roofing system or old roofing refurbishment of refrigeration houses,public buildings, and large-span factories that have high requirements upon temperature and humidity.
Note: Application for underground or concealed waterproofing projects is not recommended.
Advantages
- Ozone resistance, durable and weldable
- No containing plasticizer, because of no plasticizer oozing out, prolongs service life
- No chlorinated polymer or chlorine. no chlorine is emitted during welding operation and installation process, so to keep people's health and the environment green
- Superior low-temperature flexibility, no embrittlement occurs under-40ºC, long-term good performance under circumstances of -60ºCto-135ºC
- Withstand against chemicals and microorganisms eroding,
- Sable light color (mainly white) and smooth surface showcase high reflectivity
- High reflectivity and strong contamination resistance
- Environment friendly, can be recyclable
| NO. | Item | Value | |||
| Smooth one (Category H) | Fiber fleece- backed (Category L) | Reinforced with polyester scrim (Category P) | |||
| 1 | Thickness of resin attaching to embedded scrim/ mm ≥ | ---------- | ---------- | 0.4 | |
| 2 | Tensile property | Max tensile force / N/cm ≥ | ---------- | 120 | 250 |
| Tensile strength/ MPa ≥ | 12.0 | ---------- | ---------- | ||
| Elongation at break/ % ≥ | 500 | 250 | --------- | ||
| 3 | Dimensional variation after heating/ 100% ≤ | 2.0 | 1.0 | 0.5 | |
| 4 | Low temperature flexibility | -40ºC (no crack) | |||
| 5 | Impermeability | 0.3MPa, 2h , impermeable | |||
| 6 | Compression resistance | 0.5kg.m (no penetration) | |||
| 7 | Tear strength of overlapping / N/mm ≥ | 4.0 | 3.0 | ||
| 8 | Water absorption (70 ºC 168h) / % ≤ | 4.0 | |||
| 9 | Heat aging (80ºC) | Time duration | 672h | ||
| Appearance | No bubble, crack, delamination, or pinhole | ||||
| Retention rate of max tensile force / % ≥ | ---------- | 90 | 90 | ||
| Retention rate of tensile strength / % ≥ | 90 | ---------- | ---------- | ||
| Retention rate of elongation at break/ % ≥ | 90 | 90 | ---------- | ||
| Low temperature flexibility | -40ºC (no crack) | ||||
| 10 | Chemical resistance | Appearance | No bubble, crack, delamination, or pinhole | ||
| Retention rate of max tensile force / % ≥ | ---------- | 90 | 90 | ||
| Retention rate of tensile strength/ % ≥ | 90 | ---------- | ---------- | ||
| Retention rate of elongation at break/ % ≥ | 90 | 90 | ---------- | ||
| Low temperature flexibility | -40ºC (no crack) | ||||
| 11 | Artificial Weathering | Time duration | 1500hb) | ||
| Appearance | No bubble, crack, delamination, or pinhole | ||||
| Retention rate of max tensile force / % ≥ | ---------- | 90 | 90 | ||
| Retention rate of tensile strength / % ≥ | 90 | ---------- | ---------- | ||
| Retention rate of elongation at break / ≥ | 90 | 90 | ---------- | ||
| Low temperature flexibility | -40ºC (no crack) | ||||